SABIC Innovative Plastics LNP LUBRILOY K2000 Acetal (Asia Pacific)

Category Polymer , Thermoplastic , Acetal (POM)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP Lubriloy
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP LUBRILOY K2000 Acetal (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP LUBRILOY* K2000 is a compound based on Acetal resin containing Proprietary Lubricant. Added features of this material include: Internally Lubricated.
Physical Properties Metric English Comments
Density 1.40 g/cc
0.0506 lb/in³
ASTM D792
1.40 g/cc
0.0506 lb/in³
ISO 1183
Moisture Absorption 0.330 %
0.330 %
50% RH, 24 hrs; ASTM D570
Linear Mold Shrinkage, Flow 0.022 cm/cm

@Time 86400 sec
0.022 in/in

@Time 24.0 hour
ASTM D955
0.0221 cm/cm

@Time 86400 sec
0.0221 in/in

@Time 24.0 hour
ISO 294
Linear Mold Shrinkage, Transverse 0.0214 cm/cm

@Time 86400 sec
0.0214 in/in

@Time 24.0 hour
ISO 294
0.023 cm/cm

@Time 86400 sec
0.023 in/in

@Time 24.0 hour
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 51.0 MPa
7400 psi
ASTM D638
59.0 MPa
8560 psi
ISO 527
Tensile Strength, Yield 55.0 MPa
7980 psi
ASTM D638
60.0 MPa
8700 psi
ISO 527
Elongation at Break 13.3 %
13.3 %
ISO 527
32.4 %
32.4 %
ASTM D638
Elongation at Yield 9.0 %
9.0 %
ISO 527
9.3 %
9.3 %
ASTM D638
Tensile Modulus 2.06 GPa
299 ksi
50 mm/min; ASTM D638
2.56 GPa
371 ksi
1 mm/min; ISO 527
Flexural Strength 65.0 MPa
9430 psi
ISO 178
84.0 MPa
12200 psi
ASTM D790
Flexural Modulus 2.42 GPa
351 ksi
ASTM D790
2.42 GPa
351 ksi
ISO 178
Izod Impact, Notched 0.690 J/cm
1.29 ft-lb/in
ASTM D256
Izod Impact, Unnotched 13.56 J/cm
25.40 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 6.00 kJ/m²
2.86 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 48.0 kJ/m²
22.8 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 6.00 J
4.43 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Coefficient of Friction, Dynamic 0.38
0.38
ASTM D3702 Modified
Coefficient of Friction, Static 0.24
0.24
ASTM D3702 Modified
K (wear) Factor 20.1 x 10-8 mm³/N-M
10.0 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D3702 Modified
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 115 µm/m-°C

@Temperature -40.0 - 40.0 °C
63.9 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
115 µm/m-°C

@Temperature -40.0 - 40.0 °C
63.9 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 111 µm/m-°C

@Temperature -40.0 - 40.0 °C
61.7 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
111 µm/m-°C

@Temperature -40.0 - 40.0 °C
61.7 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 158 °C

@Thickness 3.20 mm
316 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 87.0 °C
189 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
110 °C

@Thickness 3.20 mm
230 °F

@Thickness 0.126 in
unannealed; ASTM D648