SABIC Innovative Plastics LNP LUBRILOY R2000A PA 66 (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Nylon , Nylon 66
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP Lubriloy
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP LUBRILOY R2000A PA 66 (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP LUBRILOY* R2000A is a compound based on Nylon 66 resin containing Proprietary Lubricant. Added features of this material include: Internally Lubricated.
Physical Properties Metric English Comments
Density 1.02 g/cc
0.0368 lb/in³
ASTM D792
1.02 g/cc
0.0368 lb/in³
ISO 1183
Moisture Absorption 0.300 %
0.300 %
50% RH, 24 hrs; ASTM D570
0.430 %
0.430 %
23°C / 50% RH; ISO 62
Linear Mold Shrinkage, Flow 0.0257 cm/cm

@Time 86400 sec
0.0257 in/in

@Time 24.0 hour
ISO 294
0.026 cm/cm

@Time 86400 sec
0.026 in/in

@Time 24.0 hour
ASTM D955
Linear Mold Shrinkage, Transverse 0.026 cm/cm

@Time 86400 sec
0.026 in/in

@Time 24.0 hour
ASTM D955
0.026 cm/cm

@Time 86400 sec
0.026 in/in

@Time 24.0 hour
ISO 294
Mechanical Properties Metric English Comments
Tensile Strength at Break 43.0 MPa
6240 psi
ASTM D638
43.0 MPa
6240 psi
ISO 527
Tensile Strength, Yield 43.0 MPa
6240 psi
ISO 527
47.0 MPa
6820 psi
ASTM D638
Elongation at Break 29.6 %
29.6 %
ISO 527
38.6 %
38.6 %
ASTM D638
Elongation at Yield 6.0 %
6.0 %
ASTM D638
8.8 %
8.8 %
ISO 527
Tensile Modulus 1.99 GPa
289 ksi
50 mm/min; ASTM D638
2.10 GPa
305 ksi
1 mm/min; ISO 527
Flexural Strength 67.0 MPa
9720 psi
ASTM D790
69.0 MPa
10000 psi
ISO 178
Flexural Modulus 1.93 GPa
280 ksi
ASTM D790
2.20 GPa
319 ksi
ISO 178
Izod Impact, Notched 0.740 J/cm
1.39 ft-lb/in
ASTM D256
Izod Impact, Unnotched NB
NB
ASTM D4812
Izod Impact, Notched (ISO) 6.00 kJ/m²
2.86 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 137 kJ/m²
65.2 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 6.00 J
4.43 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Impact Test 1.00 J
0.738 ft-lb
Multiaxial Impact; ISO 6603
Coefficient of Friction, Dynamic 0.31
0.31
ASTM D3702 Modified
Coefficient of Friction, Static 0.27
0.27
ASTM D3702 Modified
K (wear) Factor 24.2 x 10-8 mm³/N-M
12.0 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D3702 Modified
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 66.0 °C

@Thickness 3.20 mm
151 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 67.0 °C
153 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
62.0 °C

@Thickness 3.20 mm
144 °F

@Thickness 0.126 in
unannealed; ASTM D648
Flammability, UL94 HB

@Thickness 1.50 mm
HB

@Thickness 0.0591 in
UL 94 by SABIC-IP