SABIC Innovative Plastics LNP LUBRILOY RF208 PA 66 (Asia Pacific)
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP Lubriloy |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRILOY RF208 PA 66 (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP LUBRILOY* RF208 is a compound based on Nylon 66 resin containing Glass Fiber, Proprietary Lubricant. Added features of this material include: Internally Lubricated.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.34 g/cc | 0.0484 lb/in³ | ASTM D792 |
| 1.34 g/cc | 0.0484 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.270 % | 0.270 % | 50% RH, 24 hrs; ASTM D570 |
| 0.400 % | 0.400 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm @Time 86400 sec |
0.0040 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0041 cm/cm @Time 86400 sec |
0.0041 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0108 cm/cm @Time 86400 sec |
0.0108 in/in @Time 24.0 hour |
ISO 294 |
| 0.011 cm/cm @Time 86400 sec |
0.011 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 136 MPa | 19700 psi | ISO 527 |
| 139 MPa | 20200 psi | ASTM D638 | |
| Elongation at Break | 2.5 % | 2.5 % | ASTM D638 |
| 2.7 % | 2.7 % | ISO 527 | |
| Tensile Modulus | 10.5 GPa | 1520 ksi | 1 mm/min; ISO 527 |
| 12.34 GPa | 1790 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 200 MPa | 29000 psi | ASTM D790 |
| 211 MPa | 30600 psi | ISO 178 | |
| Flexural Modulus | 9.03 GPa | 1310 ksi | ASTM D790 |
| 11.3 GPa | 1640 ksi | ISO 178 | |
| Izod Impact, Notched | 1.33 J/cm | 2.49 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 7.20 J/cm | 13.5 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 13.0 kJ/m² | 6.19 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 55.0 kJ/m² | 26.2 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 10.0 J | 7.38 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 3.00 J | 2.21 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.41 | 0.41 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.29 | 0.29 | ASTM D3702 Modified |
| K (wear) Factor | 109 x 10-8 mm³/N-M | 54.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 238 °C | 460 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 241 °C @Thickness 3.20 mm |
466 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Polimeri Europa Edistir N 1840 Polystyrene
- PolyOne Elastamax™ XL-2175 Thermoplastic Polyolefin Elastomer (TPO (POE))
- Global ABS-1805 General Purpose ABS (discontinued **)
- Materion Beryllium Copper Alloy M25 Wire; 1/2HT (TH02) Temper; 1.3-12.7 mm Diameter (UNS C17300)
- Solvay MIRACARE® BC-34 Surfactant
- A. Schulman POLYFORT™ FXP 1943 CaC03 and Glass Fiber Hybrid Copolymer Polypropylene
- A. Schulman POLYFORT™ FPP 809 Talc Filled Homopolymer Polypropylene
- CPC - Vycom VINTEC® II TYPE II PVC Polyvinyl Chloride (PVC)
- Arkema Group OREVAC® 18732 Grafted Maleic Anhydride Polypropylene
- 3M FM282 Indoor UL Recognized White Polyester Label Products
Copyright © lookpolymers.com All Rights Reserved