SABIC Innovative Plastics LNP Lubricomp KFL22 Acetal Copolymer

Category Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer + Glass/PTFE
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP Lubricomp KFL22 Acetal Copolymer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Lubricomp* KFL22 is a compound based on Acetal Copolymer resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated.This data was supplied by SABIC-IP for the Americas region.
Physical Properties Metric English Comments
Density 1.53 g/cc
0.0553 lb/in³
ASTM D 792
Linear Mold Shrinkage, Flow 0.0080 cm/cm

@Time 86400 sec
0.0080 in/in

@Time 24.0 hour
ASTM D 955
Mechanical Properties Metric English Comments
Tensile Strength at Break 82.0 MPa
11900 psi
ASTM D 638
Elongation at Break 3.1 %
3.1 %
ASTM D 638
Tensile Modulus 5.08 GPa
737 ksi
50 mm/min; ASTM D 638
Flexural Strength 124 MPa
18000 psi
ASTM D 790
Flexural Modulus 4.90 GPa
711 ksi
ASTM D 790
Izod Impact, Notched 0.580 J/cm

@Temperature 23.0 °C
1.09 ft-lb/in

@Temperature 73.4 °F
ASTM D 256
Izod Impact, Unnotched 5.07 J/cm

@Temperature 23.0 °C
9.50 ft-lb/in

@Temperature 73.4 °F
ASTM D 4812
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 162 °C

@Thickness 3.20 mm
324 °F

@Thickness 0.126 in
unannealed; ASTM D 648