SABIC Innovative Plastics LNP Lubricomp RFL16S PA 66 (Asia Pacific)

Category Polymer , Thermoplastic , Nylon , Nylon 66
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP LUBRICOMP
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP Lubricomp RFL16S PA 66 (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Lubricomp* RFL16S is a compound based on Nylon 66 resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated, Heat Stabilized.This data was supplied by SABIC-IP for the Asia Pacific region.
Physical Properties Metric English Comments
Density 1.43 g/cc
0.0517 lb/in³
ASTM D 792
Mechanical Properties Metric English Comments
Tensile Strength at Break 183 MPa
26500 psi
ASTM D 638
Elongation at Break 3.2 %
3.2 %
ASTM D 638
Flexural Strength 268 MPa
38900 psi
ASTM D 790
Flexural Modulus 9.30 GPa
1350 ksi
ASTM D 790
Izod Impact, Notched 1.12 J/cm

@Temperature 23.0 °C
2.10 ft-lb/in

@Temperature 73.4 °F
ASTM D 256
Izod Impact, Unnotched 10.68 J/cm

@Temperature 23.0 °C
20.01 ft-lb/in

@Temperature 73.4 °F
ASTM D 4812
Coefficient of Friction, Dynamic 0.62
0.62
ASTM D 3702 Modified
Coefficient of Friction, Static 0.52
0.52
ASTM D 3702 Modified
K (wear) Factor 24.2 x 10-8 mm³/N-M
12.0 x 10-10 in³-min/ft-lb-hr
Washer; ASTM D 3702 Modified
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 254 °C

@Thickness 3.20 mm
489 °F

@Thickness 0.126 in
unannealed; ASTM D 648