SABIC Innovative Plastics LNP STAT-KON DD0009 PC

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP STAT-KON
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP STAT-KON DD0009 PC.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* STAT-KON* DD0009 is a compound based on Polycarbonate resin containing Carbon Powder. Added features of this material include: Electrically Conductive, Flame Retardant.
Physical Properties Metric English Comments
Density 1.32 g/cc
0.0477 lb/in³
ASTM D792
Moisture Absorption 0.180 %
0.180 %
50% RH, 24 hrs; ASTM D570
0.270 %
0.270 %
23°C / 50% RH; ISO 62
Linear Mold Shrinkage, Flow 0.0075 cm/cm

@Time 86400 sec
0.0075 in/in

@Time 24.0 hour
ISO 294
0.0080 cm/cm

@Time 86400 sec
0.0080 in/in

@Time 24.0 hour
ASTM D955
Linear Mold Shrinkage, Transverse 0.0070 cm/cm

@Time 86400 sec
0.0070 in/in

@Time 24.0 hour
ASTM D955
0.0072 cm/cm

@Time 86400 sec
0.0072 in/in

@Time 24.0 hour
ISO 294
Mechanical Properties Metric English Comments
Tensile Strength at Break 53.0 MPa
7690 psi
ASTM D638
57.0 MPa
8270 psi
ISO 527
Tensile Strength, Yield 61.0 MPa
8850 psi
ASTM D638
62.0 MPa
8990 psi
ISO 527
Elongation at Break 5.6 %
5.6 %
ASTM D638
7.5 %
7.5 %
ISO 527
Elongation at Yield 1.2 %
1.2 %
ASTM D638
4.1 %
4.1 %
ISO 527
Tensile Modulus 2.81 GPa
408 ksi
1 mm/min; ISO 527
2.82 GPa
409 ksi
50 mm/min; ASTM D638
Flexural Strength 102 MPa
14800 psi
ISO 178
108 MPa
15700 psi
ASTM D790
Flexural Modulus 2.82 GPa
409 ksi
ASTM D790
2.88 GPa
418 ksi
ISO 178
Izod Impact, Notched 0.680 J/cm
1.27 ft-lb/in
ASTM D256
Izod Impact, Unnotched 15.56 J/cm
29.15 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 6.00 kJ/m²
2.86 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 70.0 kJ/m²
33.3 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 10.0 J
7.38 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Impact Test 5.00 J
3.69 ft-lb
Multiaxial Impact; ISO 6603
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 53.6 µm/m-°C

@Temperature -40.0 - 40.0 °C
29.8 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
53.6 µm/m-°C

@Temperature -40.0 - 40.0 °C
29.8 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 56.7 µm/m-°C

@Temperature -40.0 - 40.0 °C
31.5 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
56.7 µm/m-°C

@Temperature -40.0 - 40.0 °C
31.5 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 139 °C
282 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
141 °C

@Thickness 3.20 mm
286 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 131 °C
268 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
132 °C

@Thickness 3.20 mm
270 °F

@Thickness 0.126 in
unannealed; ASTM D648
Flammability, UL94 V-0

@Thickness 1.70 mm
V-0

@Thickness 0.0669 in
UL 94 by SABIC-IP
Electrical Properties Metric English Comments
Surface Resistance 10000 - 1.00e+6 ohm
10000 - 1.00e+6 ohm
ASTM D257