SABIC Innovative Plastics LNP STAT-KON DD0009E PC

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP STAT-KON
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP STAT-KON DD0009E PC.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* STAT-KON* DD0009E is a compound based on Polycarbonate resin containing Carbon Powder. Added features of this material include: Electrically Conductive, Flame Retardant, Easy Molding.
Physical Properties Metric English Comments
Specific Gravity 1.32 g/cc
1.32 g/cc
ASTM D792
Density 1.32 g/cc
0.0477 lb/in³
ISO 1183
Moisture Absorption 0.160 %
0.160 %
50% RH, 24 hrs; ASTM D570
0.240 %
0.240 %
23°C / 50% RH; ISO 62
Linear Mold Shrinkage, Flow 0.0040 - 0.0060 cm/cm

@Time 86400 sec
0.0040 - 0.0060 in/in

@Time 24.0 hour
ASTM D955
Linear Mold Shrinkage, Transverse 0.0060 - 0.0080 cm/cm

@Time 86400 sec
0.0060 - 0.0080 in/in

@Time 24.0 hour
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 61.0 MPa
8850 psi
Type I, 5 mm/min; ASTM D638
Tensile Strength, Yield 61.0 MPa
8850 psi
Type I, 5 mm/min; ASTM D638
63.0 MPa
9140 psi
5 mm/min; ISO 527
Elongation at Break 4.1 %
4.1 %
Type I, 5 mm/min; ASTM D638
8.6 %
8.6 %
5 mm/min; ISO 527
Elongation at Yield 3.8 %
3.8 %
Type I, 5 mm/min; ASTM D638
4.3 %
4.3 %
5 mm/min; ISO 527
Tensile Modulus 3.05 GPa
442 ksi
50 mm/min; ASTM D638
3.05 GPa
442 ksi
1 mm/min; ISO 527
Flexural Strength 105 MPa
15200 psi
ISO 178
Flexural Yield Strength 107 MPa
15500 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 2.89 GPa
419 ksi
2 mm/min; ISO 178
3.05 GPa
442 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 0.520 J/cm
0.974 ft-lb/in
ASTM D256
Izod Impact, Unnotched 20.39 J/cm
38.20 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 5.00 kJ/m²
2.38 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 99.0 kJ/m²
47.1 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 12.0 J

@Temperature 23.0 °C
8.85 ft-lb

@Temperature 73.4 °F
ASTM D3763
Impact Test 5.00 J
3.69 ft-lb
Multiaxial Impact; ISO 6603
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 7.00 µm/m-°C

@Temperature -30.0 - 30.0 °C
3.89 µin/in-°F

@Temperature -22.0 - 86.0 °F
ASTM D696
CTE, linear, Transverse to Flow 7.00 µm/m-°C

@Temperature -30.0 - 30.0 °C
3.89 µin/in-°F

@Temperature -22.0 - 86.0 °F
ASTM D696
Deflection Temperature at 0.46 MPa (66 psi) 141 °C
286 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
141 °C

@Thickness 3.20 mm
286 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 128 °C
262 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
130 °C

@Thickness 3.20 mm
266 °F

@Thickness 0.126 in
unannealed; ASTM D648
Electrical Properties Metric English Comments
Surface Resistance 2.0 - 4.0 ohm
2.0 - 4.0 ohm
ASTM D257