SABIC Innovative Plastics LNP STAT-KON DD200C PC (Asia Pacific)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON DD200C PC (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PTFE free polycarbonate compounds with ESD safety and good lubricating perfomrance , suitable for Semiconductor and Hard Disk Drive (HDD) and semicon industry. Added features of this material include: Good cleanliness control, low LPC, low ionic, and low outgassing.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.22 g/cc | 1.22 g/cc | ASTM D792 |
| Density | 1.20 g/cc | 0.0434 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 46.0 MPa | 6670 psi | Type I, 5 mm/min; ASTM D638 |
| 53.0 MPa | 7690 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 53.0 MPa | 7690 psi | Type I, 5 mm/min; ASTM D638 |
| 53.0 MPa | 7690 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 10 % | 10 % | Type I, 5 mm/min; ASTM D638 |
| 10 % | 10 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 5.2 % | 5.2 % | 5 mm/min; ISO 527 |
| 5.3 % | 5.3 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 2.34 GPa | 339 ksi | 1 mm/min; ISO 527 |
| 2.40 GPa | 348 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 87.0 MPa | 12600 psi | ASTM D790 |
| Flexural Yield Strength | 87.0 MPa | 12600 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 2.20 GPa | 319 ksi | ASTM D790 |
| 2.38 GPa | 345 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 1.15 J/cm | 2.15 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 18.0 J/cm | 33.7 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² | 4.76 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 90.0 kJ/m² | 42.8 ft-lb/in² | 80*10*4; ISO 180/1U |
| Charpy Impact Unnotched | 9.20 J/cm² | 43.8 ft-lb/in² | ISO 179/2C |
| Charpy Impact, Notched | 0.900 J/cm² | 4.28 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 138 °C @Thickness 3.20 mm |
280 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 125 °C @Thickness 3.20 mm |
257 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 1e+05 - 1.00e+9 ohm | 1e+05 - 1.00e+9 ohm | ASTM D257 |
| Static Decay | 0.10 sec | 0.10 sec | 5000V to <50V; FTMS101B |