SABIC Innovative Plastics LNP STAT-KON DE003ER PC

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP STAT-KON
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP STAT-KON DE003ER PC.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP STAT-KON* DE003ER is a compound based on Polycarbonate resin containing 15% Carbon Fiber. Added features of this material include: Easy Molding. Mold Release, Statically Conductive.
Physical Properties Metric English Comments
Density 1.24 g/cc
0.0448 lb/in³
ASTM D792
1.24 g/cc
0.0448 lb/in³
ISO 1183
Moisture Absorption 0.160 %
0.160 %
50% RH, 24 hrs; ASTM D570
Linear Mold Shrinkage, Flow 0.00040 - 0.0010 cm/cm

@Time 86400 sec
0.00040 - 0.0010 in/in

@Time 24.0 hour
ASTM D955
0.00040 - 0.0013 cm/cm

@Time 86400 sec
0.00040 - 0.0013 in/in

@Time 24.0 hour
ISO 294
Linear Mold Shrinkage, Transverse 0.0030 - 0.0040 cm/cm

@Time 86400 sec
0.0030 - 0.0040 in/in

@Time 24.0 hour
ASTM D955
0.0032 - 0.0041 cm/cm

@Time 86400 sec
0.0032 - 0.0041 in/in

@Time 24.0 hour
ISO 294
Mechanical Properties Metric English Comments
Tensile Strength at Break 108 MPa
15700 psi
ISO 527
109 MPa
15800 psi
ASTM D638
Elongation at Break 2.0 %
2.0 %
ISO 527
2.1 %
2.1 %
ASTM D638
Tensile Modulus 8.41 GPa
1220 ksi
1 mm/min; ISO 527
8.78 GPa
1270 ksi
50 mm/min; ASTM D638
Flexural Strength 176 MPa
25500 psi
ISO 178
182 MPa
26400 psi
ASTM D790
Flexural Modulus 7.79 GPa
1130 ksi
ASTM D790
8.04 GPa
1170 ksi
ISO 178
Izod Impact, Notched 0.740 J/cm
1.39 ft-lb/in
ASTM D256
Izod Impact, Unnotched 4.91 J/cm
9.20 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 6.00 kJ/m²
2.86 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 33.0 kJ/m²
15.7 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 15.0 J
11.1 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Impact Test 3.00 J
2.21 ft-lb
Multiaxial Impact; ISO 6603
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 17.6 µm/m-°C

@Temperature -40.0 - 40.0 °C
9.78 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
17.7 µm/m-°C

@Temperature -40.0 - 40.0 °C
9.83 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 50.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
27.8 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
50.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
27.8 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 145 °C

@Thickness 3.20 mm
293 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 145 °C
293 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
137 °C

@Thickness 3.20 mm
279 °F

@Thickness 0.126 in
unannealed; ASTM D648
Electrical Properties Metric English Comments
Surface Resistance 100 ohm - 1e+05
100 ohm - 1e+05
ASTM D257