- SABIC Innovative Plastics LNP STAT-KON DX89795 PC (Europe-Africa-Middle East)
SABIC Innovative Plastics LNP STAT-KON DX89795 PC (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON DX89795 PC (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* STATKON* DX89795 is a compound based on Polycarbone resin containing Carbon Powder. Added features include: Electrically Conductive, Easy Molding, Mold Release.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.24 g/cc | 0.0448 lb/in³ | ISO 1183 |
| Water Absorption | 0.34 % @Time 86400 sec |
0.34 % @Time 24.0 hour |
ISO 62-1 |
| Linear Mold Shrinkage, Flow | 0.0060 cm/cm | 0.0060 in/in | SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 58.0 MPa | 8410 psi | 5 mm/min; ISO 527 |
| Elongation at Yield | 4.8 % | 4.8 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 2.60 GPa | 377 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 95.0 MPa | 13800 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 2.50 GPa | 363 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² | 4.76 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 135 kJ/m² | 64.2 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 70.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
38.9 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 72.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
40.0 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 126 °C | 259 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| UL RTI, Electrical | 80.0 °C | 176 °F | UL 746B |
| UL RTI, Mechanical with Impact | 80.0 °C | 176 °F | UL 746B |
| UL RTI, Mechanical without Impact | 80.0 °C | 176 °F | UL 746B |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 1000 ohm - 1e+05 | 1000 ohm - 1e+05 | ASTM D257 |
Users viewing this material also viewed the following:
- Kolon SPESIN® KP210 General Purpose PBT Resin (discontinued **)
- Lucite International Lucite® 41 Acrylic Resin for Casting and Embedments
- Indium Corp. 16-1085 Flux Thinner
- Teknor Apex APEX® 3090-H Polyvinyl Chloride, Flexible
- SABIC Innovative Plastics LNP THERMOCOMP WC003 PBT (Europe-Africa-Middle East)
- DuPont Teijin Films Mylar® M34 Polyester Film, 50 Gauge (13 µm), PVDC Coated
- AorTech Biomaterials ECSil™ 60D Biomedical Carbonate Silicone Pellets
- 3M Controltac™ IJ380Cv3 Wrap Film with Comply™ v3 Adhesive
Copyright © lookpolymers.com All Rights Reserved