SABIC Innovative Plastics LNP STAT-KON Lexan_LCF1506 PC (Asia Pacific)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON Lexan_LCF1506 PC (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
15% carbon fiber, 6% PTFE reinforced polycarbonate.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.31 g/cc | 1.31 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.00050 - 0.0015 cm/cm @Thickness 3.20 mm |
0.00050 - 0.0015 in/in @Thickness 0.126 in |
SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0020 - 0.0030 cm/cm @Thickness 3.20 mm |
0.0020 - 0.0030 in/in @Thickness 0.126 in |
SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 111 MPa | 16100 psi | Type I, 5 mm/min; ASTM D638 |
| Tensile Strength, Yield | 111 MPa | 16100 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 4.1 % | 4.1 % | Type I, 5 mm/min; ASTM D638 |
| Flexural Strength | 154 MPa | 22300 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
| 160 MPa | 23200 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 8.41 GPa | 1220 ksi | 2.6 mm/min, 100 mm span; ASTM D790 |
| 9.08 GPa | 1320 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.530 J/cm | 0.993 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 2.83 J/cm | 5.30 ft-lb/in | ASTM D4812 |
| Dart Drop, Total Energy | 11.0 J | 8.11 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Coefficient of Friction, Dynamic | 0.19 | 0.19 | steel; ASTM D1894 |
| Coefficient of Friction, Static | 0.41 | 0.41 | steel; ASTM D1894 |
| K (wear) Factor | 2010 x 10-8 mm³/N-M | 1000 x 10-10 in³-min/ft-lb-hr | PV=2000 psi-fpm vs Self; SABIC Method |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 141 °C @Thickness 3.20 mm |
286 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| 144 °C @Thickness 6.40 mm |
291 °F @Thickness 0.252 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 137 °C @Thickness 3.20 mm |
279 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| 139 °C @Thickness 6.40 mm |
282 °F @Thickness 0.252 in |
unannealed; ASTM D648 | |
| UL RTI, Electrical | 80.0 °C | 176 °F | UL 746B |
| UL RTI, Mechanical with Impact | 80.0 °C | 176 °F | UL 746B |
| UL RTI, Mechanical without Impact | 80.0 °C | 176 °F | UL 746B |
| Flammability, UL94 | V-0 @Thickness 1.49 mm |
V-0 @Thickness 0.0587 in |
UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 10000 ohm | 10000 ohm | ASTM D257 |
| Static Decay | 0.010 sec | 0.010 sec | 5000V to <50V; FTMS101B |
Users viewing this material also viewed the following:
- PolyOne Nymax™ GF 1200 A 40 IM Black 13A Polyamide 66 (Nylon 66)
- Albis Plastics Cellulose Acetate Butyrate B9024 (UVI, Odor Mask Added), 10% Plasticizer (discontinued **)
- Lehmann & Voss LUVOCOM® 1800-8435 PET, with PTFE
- Teknor Apex APEX® 90-A472R-90-NT Polyvinyl Chloride, Flexible
- Cossa Polimeri ESTAPROP H 0560 GFCTG Polypropylene, 30% Mixed Filler
- ChevronTexaco EP 1 Aluminum Complex
- BryCoat WS2 Tungsten Disulfide Coating
- Arlon 49583R010 0.0105" (0.267 mm) Cured Silicone Rubber with Fiberglass Substrate
- Toyobo GLAMIDE® T-401 Nylon-6
- ExxonMobil Exceed™ 3518 CB Premium Cast Film Resin
Copyright © lookpolymers.com All Rights Reserved