SABIC Innovative Plastics LNP STAT-KON ME003S PP

Category Polymer , Thermoplastic , Polypropylene (PP)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP STAT-KON
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP STAT-KON ME003S PP.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* STAT-KON* ME003S is a compound based on Polypropylene resin containing 15% Carbon Fiber. Added features of this material include: Electrically Conductive, Heat Stabilized.
Physical Properties Metric English Comments
Density 0.990 g/cc
0.0358 lb/in³
ASTM D792
0.990 g/cc
0.0358 lb/in³
ISO 1183
Linear Mold Shrinkage, Flow 0.0040 - 0.0060 cm/cm

@Time 86400 sec
0.0040 - 0.0060 in/in

@Time 24.0 hour
ASTM D955
0.0052 cm/cm

@Time 86400 sec
0.0052 in/in

@Time 24.0 hour
ISO 294
Linear Mold Shrinkage, Transverse 0.0050 - 0.0070 cm/cm

@Time 86400 sec
0.0050 - 0.0070 in/in

@Time 24.0 hour
ASTM D955
0.0060 cm/cm

@Time 86400 sec
0.0060 in/in

@Time 24.0 hour
ISO 294
Mechanical Properties Metric English Comments
Tensile Strength at Break 39.0 MPa
5660 psi
ASTM D638
44.0 MPa
6380 psi
ISO 527
Tensile Strength, Yield 47.0 MPa
6820 psi
ASTM D638
47.0 MPa
6820 psi
ISO 527
Elongation at Break 1.0 %
1.0 %
ISO 527
1.3 %
1.3 %
ASTM D638
Elongation at Yield 0.70 %
0.70 %
ASTM D638
0.70 %
0.70 %
ISO 527
Tensile Modulus 8.59 GPa
1250 ksi
1 mm/min; ISO 527
8.96 GPa
1300 ksi
50 mm/min; ASTM D638
Flexural Strength 62.0 MPa
8990 psi
ISO 178
65.0 MPa
9430 psi
ASTM D790
Flexural Modulus 6.89 GPa
999 ksi
ASTM D790
7.00 GPa
1020 ksi
ISO 178
Izod Impact, Notched 0.160 J/cm
0.300 ft-lb/in
ASTM D256
Izod Impact, Unnotched 1.28 J/cm
2.40 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 1.00 kJ/m²
0.476 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 8.00 kJ/m²
3.81 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 14.0 J
10.3 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Impact Test 3.00 J
2.21 ft-lb
Multiaxial Impact; ISO 6603
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 70.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
38.9 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
70.2 µm/m-°C

@Temperature -40.0 - 40.0 °C
39.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
CTE, linear, Transverse to Flow 28.8 µm/m-°C

@Temperature -40.0 - 40.0 °C
16.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
29.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
16.1 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 150 °C
302 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
153 °C

@Thickness 3.20 mm
307 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 131 °C
268 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
133 °C

@Thickness 3.20 mm
271 °F

@Thickness 0.126 in
unannealed; ASTM D648
Electrical Properties Metric English Comments
Surface Resistance 100 ohm
100 ohm
ASTM D257