SABIC Innovative Plastics LNP STAT-KON Noryl_HMC202M PPE+PS

Category Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP STAT-KON
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP STAT-KON Noryl_HMC202M PPE+PS.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
DATA ON BK1005 ONLY.
Physical Properties Metric English Comments
Specific Gravity 1.18 g/cc
1.18 g/cc
ASTM D792
Linear Mold Shrinkage, Flow 0.0010 - 0.0030 cm/cm

@Thickness 3.20 mm
0.0010 - 0.0030 in/in

@Thickness 0.126 in
SABIC Method
Linear Mold Shrinkage, Transverse 0.0040 - 0.0060 cm/cm

@Thickness 3.20 mm
0.0040 - 0.0060 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 7.6 g/10 min

@Load 5.00 kg,
Temperature 300 °C
7.6 g/10 min

@Load 11.0 lb,
Temperature 572 °F
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 86.0 MPa
12500 psi
5 mm/min; ISO 527
96.0 MPa
13900 psi
Type I, 5 mm/min; ASTM D638
Tensile Strength, Yield 86.0 MPa
12500 psi
5 mm/min; ISO 527
96.0 MPa
13900 psi
Type I, 5 mm/min; ASTM D638
Elongation at Break 4.1 %
4.1 %
Type I, 5 mm/min; ASTM D638
Elongation at Yield 4.1 %
4.1 %
Type I, 5 mm/min; ASTM D638
Tensile Modulus 7.58 GPa
1100 ksi
5 mm/min; ASTM D638
Flexural Strength 135 MPa
19600 psi
1.3 mm/min, 50 mm span; ASTM D790
145 MPa
21000 psi
2 mm/min; ISO 178
Flexural Yield Strength 145 MPa
21000 psi
2 mm/min; ISO 178
Flexural Modulus 6.89 GPa
999 ksi
1.3 mm/min, 50 mm span; ASTM D790
7.15 GPa
1040 ksi
2 mm/min; ISO 178
Izod Impact, Notched 0.420 J/cm
0.787 ft-lb/in
ASTM D256
Izod Impact, Unnotched 2.67 J/cm
5.00 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 4.00 kJ/m²
1.90 ft-lb/in²
80*10*4; ISO 180/1A
Dart Drop, Total Energy 9.00 J

@Temperature 23.0 °C
6.64 ft-lb

@Temperature 73.4 °F
ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 13.0 µm/m-°C

@Temperature 23.0 - 150 °C
7.22 µin/in-°F

@Temperature 73.4 - 302 °F
ISO 11359-2
61.2 µm/m-°C

@Temperature -30.0 - 30.0 °C
34.0 µin/in-°F

@Temperature -22.0 - 86.0 °F
ASTM D696
CTE, linear, Transverse to Flow 57.0 µm/m-°C

@Temperature 23.0 - 150 °C
31.7 µin/in-°F

@Temperature 73.4 - 302 °F
ISO 11359-2
158 µm/m-°C

@Temperature -30.0 - 30.0 °C
87.8 µin/in-°F

@Temperature -22.0 - 86.0 °F
ASTM D696
Deflection Temperature at 0.46 MPa (66 psi) 177 °C

@Thickness 3.20 mm
351 °F

@Thickness 0.126 in
unannealed; ASTM D648
181 °C

@Thickness 6.40 mm
358 °F

@Thickness 0.252 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 177 °C
351 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
171 °C

@Thickness 3.20 mm
340 °F

@Thickness 0.126 in
unannealed; ASTM D648
173 °C

@Thickness 6.40 mm
343 °F

@Thickness 0.252 in
unannealed; ASTM D648
Vicat Softening Point 180 °C
356 °F
Rate B/50; ASTM D1525
180 °C
356 °F
Rate B/120; ISO 306
UL RTI, Electrical 50.0 °C
122 °F
UL 746B
UL RTI, Mechanical with Impact 50.0 °C
122 °F
UL 746B
UL RTI, Mechanical without Impact 50.0 °C
122 °F
UL 746B
Flammability, UL94 V-1

@Thickness 1.49 mm
V-1

@Thickness 0.0587 in
UL 94
Electrical Properties Metric English Comments
Surface Resistance 10000 ohm
10000 ohm
ASTM D257