SABIC Innovative Plastics LNP STAT-KON OEL13I PPS - Linear
| Category | Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP STAT-KON OEL13I PPS - Linear.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* STAT-KON* OEL13I is a compound based on PPS-Linear resin containing 15% Carbon Fiber, 5% PTFE. Added features of this grade include: High Impact, Wear Resistant, Electrically Conductive.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.37 g/cc | 0.0495 lb/in³ | ASTM D792 |
| 1.37 g/cc | 0.0495 lb/in³ | ISO 1183 | |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0040 cm/cm @Time 86400 sec |
0.0020 - 0.0040 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0070 - 0.0090 cm/cm @Time 86400 sec |
0.0070 - 0.0090 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 130 MPa | 18900 psi | 5 mm/min; ISO 527 |
| 132 MPa | 19100 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 1.4 % | 1.4 % | 5 mm/min; ISO 527 |
| 1.8 % | 1.8 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 13.95 GPa | 2023 ksi | 50 mm/min; ASTM D638 |
| 16.59 GPa | 2406 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 195 MPa | 28300 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 218 MPa | 31600 psi | ISO 178 | |
| Flexural Modulus | 10.51 GPa | 1524 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 11.92 GPa | 1729 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.930 J/cm | 1.74 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 6.01 J/cm | 11.3 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 8.00 kJ/m² | 3.81 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 35.0 kJ/m² | 16.7 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 16.0 J @Temperature 23.0 °C |
11.8 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 3.00 J | 2.21 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 14.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
7.78 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 60.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
33.3 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 260 °C | 500 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 273 °C @Thickness 3.20 mm |
523 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 212 °C | 414 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 213 °C @Thickness 3.20 mm |
415 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.0 - 3.0 ohm-cm | 1.0 - 3.0 ohm-cm | ASTM D257 |
| Surface Resistance | 1.0 - 3.0 ohm | 1.0 - 3.0 ohm | ROA; IEC 60093 |
| 2.0 - 4.0 ohm | 2.0 - 4.0 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- Murtfeldt Murytal® H Acetal Homopolymer
- Total Finaprene® 602 Styrene-Butadiene TPE Copolymer Compound, Formulated to 59 Shore A (discontinued **)
- LG Chemical LUMID GP1200A(W) PA6, Medium Viscosity
- Haynes 214® alloy, cold rolled annealed sheet 2.0-3.2 mm thick
- Karina E 813-18/190-Y-RT-PO Gray PVC Compound
- DSM Akulon® K224-G6-FC BK00001 PA6-GF30
- Axiall 1275 Plenum Flexible PVC
- Asia International Enterprise (Hong Kong) 60C6 Nylon 66
- Chosun Refractories WM-SN Special Mortar for Sliding Gate Valve
Copyright © lookpolymers.com All Rights Reserved