SABIC Innovative Plastics LNP STAT-KON RE002 PA 66

Category Polymer , Thermoplastic , Nylon , Nylon 66
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP STAT-KON
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP STAT-KON RE002 PA 66.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* STAT-KON* RE002 is a compound based on Nylon 66 resin containing 10% Carbon Fiber. Added features of this material include: Electrically Conductive.
Physical Properties Metric English Comments
Density 1.18 g/cc
0.0426 lb/in³
ASTM D792
1.18 g/cc
0.0426 lb/in³
ISO 1183
Moisture Absorption 0.800 %
0.800 %
50% RH, 24 hrs; ASTM D570
Linear Mold Shrinkage, Flow 0.0060 - 0.0080 cm/cm

@Time 86400 sec
0.0060 - 0.0080 in/in

@Time 24.0 hour
ASTM D955
0.0074 cm/cm

@Time 86400 sec
0.0074 in/in

@Time 24.0 hour
ISO 294
Linear Mold Shrinkage, Transverse 0.013 cm/cm

@Time 86400 sec
0.013 in/in

@Time 24.0 hour
ISO 294
0.010 - 0.030 cm/cm

@Time 86400 sec
0.010 - 0.030 in/in

@Time 24.0 hour
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 126 MPa
18300 psi
ASTM D638
131 MPa
19000 psi
ISO 527
Tensile Strength, Yield 131 MPa
19000 psi
ISO 527
134 MPa
19400 psi
ASTM D638
Elongation at Break 2.1 %
2.1 %
ISO 527
2.3 %
2.3 %
ASTM D638
Elongation at Yield 2.1 %
2.1 %
ISO 527
2.3 %
2.3 %
ASTM D638
Tensile Modulus 7.80 GPa
1130 ksi
1 mm/min; ISO 527
8.27 GPa
1200 ksi
50 mm/min; ASTM D638
Flexural Strength 191 MPa
27700 psi
ISO 178
206 MPa
29900 psi
ASTM D790
Flexural Modulus 6.00 GPa
870 ksi
ISO 178
6.89 GPa
999 ksi
ASTM D790
Izod Impact, Notched 0.260 J/cm
0.487 ft-lb/in
ASTM D256
Izod Impact, Unnotched 3.63 J/cm
6.80 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 3.00 kJ/m²
1.43 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 24.0 kJ/m²
11.4 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 5.00 J
3.69 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Impact Test 1.00 J
0.738 ft-lb
Multiaxial Impact; ISO 6603
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 82.8 µm/m-°C

@Temperature -40.0 - 40.0 °C
46.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
83.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
46.1 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 28.8 µm/m-°C

@Temperature -40.0 - 40.0 °C
16.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
29.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
16.1 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 254 °C
489 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
258 °C

@Thickness 3.20 mm
496 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 241 °C
466 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
245 °C

@Thickness 3.20 mm
473 °F

@Thickness 0.126 in
unannealed; ASTM D648
Electrical Properties Metric English Comments
Surface Resistance 10 - 1000 ohm
10 - 1000 ohm
ASTM D257