SABIC Innovative Plastics LNP Stat-kon AE0039 ABS (Asia Pacific)
| Category | Polymer , Thermoplastic , ABS Polymer |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Stat-kon AE0039 ABS (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* STAT-KON* AE0039 is a compound based on Acrylonitrile Butadiene Styrene resin containing Carbon Fiber, Flame Retardant. Added features of this material include: Electrically Conductive.This data was supplied by SABIC-IP for the Asia Pacific region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.25 g/cc | 0.0452 lb/in³ | ASTM D 792 |
| 1.26 g/cc | 0.0455 lb/in³ | ISO 1183 | |
| Moisture Absorption at Equilibrium | 0.31 % | 0.31 % | 23°C / 50% RH; ISO 62 |
| 0.30 % @Time 86400 sec |
0.30 % @Time 24.0 hour |
50% RH; ASTM D 570 | |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm @Time 86400 sec |
0.0030 in/in @Time 24.0 hour |
ASTM D 955 |
| 0.0032 cm/cm @Time 86400 sec |
0.0032 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0016 cm/cm @Time 86400 sec |
0.0016 in/in @Time 24.0 hour |
ISO 294 |
| 0.0020 cm/cm @Time 86400 sec |
0.0020 in/in @Time 24.0 hour |
ASTM D 955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 65.0 MPa | 9430 psi | ISO 527 |
| 103 MPa | 14900 psi | ASTM D 638 | |
| Elongation at Break | 1.5 % | 1.5 % | ASTM D 638 |
| 2.3 % | 2.3 % | ISO 527 | |
| Tensile Modulus | 11.23 GPa | 1629 ksi | 50 mm/min; ASTM D 638 |
| Flexural Strength | 151 MPa | 21900 psi | ASTM D 790 |
| 164 MPa | 23800 psi | ISO 178 | |
| Flexural Modulus | 8.27 GPa | 1200 ksi | ASTM D 790 |
| 9.30 GPa | 1350 ksi | ISO 178 | |
| Izod Impact, Notched | 0.210 J/cm @Temperature 23.0 °C |
0.393 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 1.48 J/cm @Temperature 23.0 °C |
2.77 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² @Temperature 23.0 °C |
1.90 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 17.0 kJ/m² @Temperature 23.0 °C |
8.09 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| 6.00 J @Temperature 23.0 °C |
4.43 ft-lb @Temperature 73.4 °F |
Instrumented Impact Energy @ peak; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 101 °C | 214 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 101 °C @Thickness 3.20 mm |
214 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
Users viewing this material also viewed the following:
- LG Chemical LUMID GP2500A(W) PA6+GF50%, General Purpose
- Greene Tweed Arlon® 1330 PEEK
- Lehmann & Voss LUVOCOM® 1105-8184 PEEK, with carbon fiber
- Silberline "A" Series A-2291FG
- Lubrizol Estane® ALR E68D-V Thermoplastic Polyurethane
- Daikin POLYFLON M-139 PTFE Molding Powder, Free Flow
- Hippe PA 12 Nylon 12
- DuPont Teijin Films Mylar® OB01 Polyester Packaging Film, 100 Gauge
- Barlog Plastics KEBATER A0230 PBT/ABS, 30% glass fiber reinforced, low warpage
- ACC QM 113 QSI Quantum Silicones 13 Durometer Condensation Cured Moldmaking Material
Copyright © lookpolymers.com All Rights Reserved