SABIC Innovative Plastics LNP Stat-kon EE008E PEI
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Stat-kon EE008E PEI.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP STAT-KON* EE008E is a compound based on Polyetherimide resin containing Carbon Fiber. Added features of this material include: Easy Molding.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.44 g/cc | 0.0520 lb/in³ | ASTM D 792 |
| 1.44 g/cc | 0.0520 lb/in³ | ISO 1183 | |
| Moisture Absorption at Equilibrium | 0.14 % | 0.14 % | 23°C / 50% RH; ISO 62 |
| 0.11 % @Time 86400 sec |
0.11 % @Time 24.0 hour |
50% RH; ASTM D 570 | |
| Linear Mold Shrinkage, Transverse | 0.00080 - 0.010 cm/cm @Time 86400 sec |
0.00080 - 0.010 in/in @Time 24.0 hour |
ASTM D 955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 183 MPa | 26500 psi | 5 mm/min; ISO 527 |
| 190 MPa | 27600 psi | Type I, 5 mm/min; ASTM D 638 | |
| Tensile Strength, Yield | 183 MPa | 26500 psi | 5 mm/min; ISO 527 |
| 189 MPa | 27400 psi | Type I, 5 mm/min; ASTM D 638 | |
| Elongation at Break | 0.80 % | 0.80 % | 5 mm/min; ISO 527 |
| 0.90 % | 0.90 % | Type I, 5 mm/min; ASTM D 638 | |
| Elongation at Yield | 0.80 % | 0.80 % | 5 mm/min; ISO 527 |
| 0.90 % | 0.90 % | Type I, 5 mm/min; ASTM D 638 | |
| Tensile Modulus | 26.32 GPa | 3817 ksi | 1 mm/min; ISO 527 |
| 28.0 GPa | 4060 ksi | 50 mm/min; ASTM D 638 | |
| Flexural Strength | 272 MPa | 39500 psi | ISO 178 |
| 297 MPa | 43100 psi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Flexural Yield Strength | 296 MPa | 42900 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Flexural Modulus | 22.76 GPa | 3301 ksi | 2 mm/min; ISO 178 |
| 24.4 GPa | 3540 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Izod Impact, Notched | 0.420 J/cm @Temperature 23.0 °C |
0.787 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 4.00 J/cm @Temperature 23.0 °C |
7.49 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 3.00 kJ/m² @Temperature 23.0 °C |
1.43 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 23.0 kJ/m² @Temperature 23.0 °C |
10.9 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Impact Test | 3.00 J | 2.21 ft-lb | Multiaxial Impact; ISO 6603 |
| 6.00 J @Temperature 23.0 °C |
4.43 ft-lb @Temperature 73.4 °F |
Instrumented Impact Total Energy; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 6.00 µm/m-°C @Temperature -30.0 - 30.0 °C |
3.33 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D 696 |
| CTE, linear, Transverse to Flow | 26.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
14.4 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D 696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 205 °C | 401 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 200 °C @Thickness 3.20 mm |
392 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 197 °C | 387 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 191 °C @Thickness 3.20 mm |
376 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 1.0 - 3.0 ohm | 1.0 - 3.0 ohm | ASTM D 257 |