SABIC Innovative Plastics LNP Stat-kon TD000
| Category | Polymer , Thermoplastic , Polyurethane, TP , Thermoplastic Polyurethane (TPUR), Carbon Fiber Reinforced |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Stat-kon TD000.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Stat-kon* TD000 is a compound based on Polyurethane resin. Added features of this material include: Electrically Conductive.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.26 g/cc | 1.26 g/cc | ASTM D 792 |
| Density | 1.26 g/cc | 0.0455 lb/in³ | ASTM D 792 |
| Moisture Absorption at Equilibrium | 0.79 % | 0.79 % | 23°C / 50% RH; ISO 62 |
| 0.50 % @Time 86400 sec |
0.50 % @Time 24.0 hour |
50% RH; ASTM D 570 | |
| Linear Mold Shrinkage, Flow | 0.010 - 0.030 cm/cm @Time 86400 sec |
0.010 - 0.030 in/in @Time 24.0 hour |
ASTM D 955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.030 cm/cm @Time 86400 sec |
0.010 - 0.030 in/in @Time 24.0 hour |
ASTM D 955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 24.0 MPa | 3480 psi | 5 mm/min; ISO 527 |
| 25.0 MPa | 3630 psi | ASTM D 638 | |
| Tensile Strength, Yield | 24.0 MPa | 3480 psi | 5 mm/min; ISO 527 |
| 26.0 MPa | 3770 psi | Type I, 50 mm/min; ASTM D 638 | |
| Elongation at Break | 140 % | 140 % | 5 mm/min; ISO 527 |
| 160 % | 160 % | ASTM D 638 | |
| Elongation at Yield | 140 % | 140 % | 5 mm/min; ISO 527 |
| 160 % | 160 % | Type I, 50 mm/min; ASTM D 638 | |
| Tensile Modulus | 0.180 GPa | 26.1 ksi | 50 mm/min; ASTM D 638 |
| 0.300 GPa | 43.5 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 6.00 MPa | 870 psi | ASTM D 790 |
| 16.0 MPa | 2320 psi | ISO 178 | |
| Flexural Modulus | 0.350 GPa | 50.8 ksi | 2 mm/min; ISO 178 |
| 0.360 GPa | 52.2 ksi | ASTM D 790 | |
| Izod Impact, Notched | 7.94 J/cm @Temperature 23.0 °C |
14.9 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 10.03 J/cm @Temperature 23.0 °C |
18.79 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 78.0 kJ/m² @Temperature 23.0 °C |
37.1 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 87.0 kJ/m² @Temperature 23.0 °C |
41.4 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Impact Test | 55.0 J | 40.6 ft-lb | Multiaxial Impact; ISO 6603 |
| 50.0 J @Temperature 23.0 °C |
36.9 ft-lb @Temperature 73.4 °F |
Instrumented Impact Total Energy; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 12.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
6.67 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D 696 |
| CTE, linear, Transverse to Flow | 14.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
7.78 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D 696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 69.0 °C | 156 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 70.0 °C @Thickness 3.20 mm |
158 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 48.0 °C | 118 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 47.0 °C @Thickness 3.20 mm |
117 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 3.0 - 5.0 ohm | 3.0 - 5.0 ohm | ASTM D 257 |