Material Notes:
LNP* Stat-loy* A3000Z is a compound based on Acrylonitrile Butadiene Styrene resin containing Anti-Static. Added features of this material include: Antistat.This data was supplied by SABIC-IP for the Americas region.
Physical Properties Metric English Comments
Density 1.05 g/cc
0.0379 lb/in³
ASTM D 792
1.05 g/cc
0.0379 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 1.6 %

@Time 86400 sec
1.6 %

@Time 24.0 hour
50% RH; ASTM D 570
Linear Mold Shrinkage, Flow 0.0077 cm/cm

@Time 86400 sec
0.0077 in/in

@Time 24.0 hour
ISO 294
0.0070 - 0.0090 cm/cm

@Time 86400 sec
0.0070 - 0.0090 in/in

@Time 24.0 hour
ASTM D 955
Linear Mold Shrinkage, Transverse 0.0080 - 0.010 cm/cm

@Time 86400 sec
0.0080 - 0.010 in/in

@Time 24.0 hour
ASTM D 955
0.0092 cm/cm

@Time 86400 sec
0.0092 in/in

@Time 24.0 hour
ISO 294
Mechanical Properties Metric English Comments
Tensile Strength at Break 24.0 MPa
3480 psi
ASTM D 638
27.0 MPa
3920 psi
ISO 527
Tensile Strength, Yield 30.0 MPa
4350 psi
ASTM D 638
36.0 MPa
5220 psi
ISO 527
Elongation at Break 50.1 %
50.1 %
ISO 527
52.1 %
52.1 %
ASTM D 638
Elongation at Yield 3.5 %
3.5 %
ASTM D 638
3.5 %
3.5 %
ISO 527
Tensile Modulus 1.37 GPa
199 ksi
50 mm/min; ASTM D 638
1.58 GPa
229 ksi
1 mm/min; ISO 527
Flexural Strength 45.0 MPa
6530 psi
ISO 178
Flexural Modulus 1.37 GPa
199 ksi
ASTM D 790
1.60 GPa
232 ksi
ISO 178
Izod Impact, Notched 3.89 J/cm

@Temperature 23.0 °C
7.29 ft-lb/in

@Temperature 73.4 °F
ASTM D 256
Izod Impact, Unnotched 14.2 J/cm

@Temperature 23.0 °C
26.6 ft-lb/in

@Temperature 73.4 °F
ASTM D 4812
Izod Impact, Notched (ISO) 32.0 kJ/m²

@Temperature 23.0 °C
15.2 ft-lb/in²

@Temperature 73.4 °F
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 148 kJ/m²

@Temperature 23.0 °C
70.4 ft-lb/in²

@Temperature 73.4 °F
80*10*4; ISO 180/1U
Impact Test 35.0 J
25.8 ft-lb
Multiaxial Impact; ISO 6603
39.0 J

@Temperature 23.0 °C
28.8 ft-lb

@Temperature 73.4 °F
Instrumented Impact Energy @ peak; ASTM D 3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 127 µm/m-°C

@Temperature -40.0 - 40.0 °C
70.6 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
128 µm/m-°C

@Temperature -40.0 - 40.0 °C
71.1 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
CTE, linear, Transverse to Flow 103 µm/m-°C

@Temperature -40.0 - 40.0 °C
57.2 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
103 µm/m-°C

@Temperature -40.0 - 40.0 °C
57.2 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 91.0 °C
196 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
86.0 °C

@Thickness 3.20 mm
187 °F

@Thickness 0.126 in
unannealed; ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 78.0 °C
172 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
73.0 °C

@Thickness 3.20 mm
163 °F

@Thickness 0.126 in
unannealed; ASTM D 648
Electrical Properties Metric English Comments
Surface Resistance 1.00e+10 - 1.00e+12 ohm
1.00e+10 - 1.00e+12 ohm
ASTM D 257