SABIC Innovative Plastics LNP THERMOCOMP 2X04505 ETFE

Category Polymer , Thermoplastic , Fluoropolymer , ETFE/ECTFE
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP THERMOCOMP
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP THERMOCOMP 2X04505 ETFE.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* THERMOCOMP* 2X04505 is a compound based on ETFE resin containing Proprietary Filler(s).
Physical Properties Metric English Comments
Density 1.74 g/cc
0.0629 lb/in³
ISO 1183
1.75 g/cc
0.0632 lb/in³
ASTM D792
Linear Mold Shrinkage, Flow 0.010 - 0.012 cm/cm

@Time 86400 sec
0.010 - 0.012 in/in

@Time 24.0 hour
ASTM D955
0.011 cm/cm

@Time 86400 sec
0.011 in/in

@Time 24.0 hour
ISO 294
Linear Mold Shrinkage, Transverse 0.018 - 0.020 cm/cm

@Time 86400 sec
0.018 - 0.020 in/in

@Time 24.0 hour
ASTM D955
0.019 cm/cm

@Time 86400 sec
0.019 in/in

@Time 24.0 hour
ISO 294
Mechanical Properties Metric English Comments
Tensile Strength at Break 85.0 MPa
12300 psi
ASTM D638
85.0 MPa
12300 psi
Type I, 5 mm/min; ASTM D638
88.0 MPa
12800 psi
ISO 527
Tensile Strength, Yield 87.0 MPa
12600 psi
ASTM D638
87.0 MPa
12600 psi
Type I, 5 mm/min; ASTM D638
89.0 MPa
12900 psi
ISO 527
Elongation at Break 4.8 %
4.8 %
ASTM D638
4.8 %
4.8 %
Type I, 5 mm/min; ASTM D638
4.9 %
4.9 %
ISO 527
Elongation at Yield 4.5 %
4.5 %
ASTM D638
4.5 %
4.5 %
Type I, 5 mm/min; ASTM D638
4.6 %
4.6 %
ISO 527
Tensile Modulus 11.58 GPa
1680 ksi
1 mm/min; ISO 527
15.16 GPa
2199 ksi
50 mm/min; ASTM D638
Flexural Strength 319 MPa
46300 psi
ISO 178
Flexural Modulus 10.34 GPa
1500 ksi
ASTM D790
10.34 GPa
1500 ksi
1.3 mm/min, 50 mm span; ASTM D790
18.8 GPa
2730 ksi
ISO 178
Izod Impact, Notched 2.72 J/cm
5.10 ft-lb/in
ASTM D256
Izod Impact, Unnotched 10.3 J/cm
19.3 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 23.0 kJ/m²
10.9 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 58.0 kJ/m²
27.6 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 18.0 J
13.3 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Impact Test 8.00 J
5.90 ft-lb
Multiaxial Impact; ISO 6603
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 77.4 µm/m-°C

@Temperature -40.0 - 40.0 °C
43.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
78.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
43.3 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 12.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
6.67 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
12.6 µm/m-°C

@Temperature -40.0 - 40.0 °C
7.00 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
Deflection Temperature at 0.46 MPa (66 psi) 251 °C
484 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
255 °C

@Thickness 3.20 mm
491 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 207 °C
405 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
222 °C

@Thickness 3.20 mm
432 °F

@Thickness 0.126 in
unannealed; ASTM D648