SABIC Innovative Plastics LNP THERMOCOMP 2Z004 ETFE
| Category | Polymer , Thermoplastic , Fluoropolymer , ETFE/ECTFE |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP 2Z004 ETFE.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* 2Z004 is a compound based on ETFE resin containing 20% Milled Glass.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.84 g/cc | 1.84 g/cc | ASTM D792 |
| Density | 1.83 g/cc | 0.0661 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.0100 % | 0.0100 % | 50% RH, 24 hrs; ASTM D570 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 21.0 MPa | 3050 psi | Type I, 5 mm/min; ASTM D638 |
| 22.0 MPa | 3190 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 27.0 MPa | 3920 psi | 5 mm/min; ISO 527 |
| 29.0 MPa | 4210 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 53 % | 53 % | Type I, 5 mm/min; ASTM D638 |
| 78 % | 78 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 22 % | 22 % | 5 mm/min; ISO 527 |
| 23 % | 23 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 1.51 GPa | 219 ksi | 1 mm/min; ISO 527 |
| 1.70 GPa | 247 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 24.0 MPa | 3480 psi | ISO 178 |
| Flexural Modulus | 1.21 GPa | 175 ksi | 2 mm/min; ISO 178 |
| 1.28 GPa | 186 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 6.15 J/cm | 11.5 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 13.4 J/cm | 25.1 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 37.0 kJ/m² | 17.6 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 119 kJ/m² | 56.6 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 26.0 J @Temperature 23.0 °C |
19.2 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 80.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
44.4 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 87.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
48.3 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 89.0 °C | 192 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 88.0 °C @Thickness 3.20 mm |
190 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 50.0 °C | 122 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 52.0 °C @Thickness 3.20 mm |
126 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Asahi Kasei Tenac® FA405 Acetal Homopolymer, Low Friction Grade (discontinued **)
- MarkeTech Gallium Arsenide Semiconductor Wafer, p-type, Zinc Doped, LEC Grown
- Imerys ImerPlastâ„¢ 15 Recycled Polyolefin for Pipe Extrusion
- KEP Kepital® FG2025 25% Glass Fiber Reinforced Acetal Copolymer
- IRPC Polimaxx Porene GA850 Acrylonitrile Butadiene Styrene
- LATI Latamid 66 H2 G/50-GWHF1 PA 66, 50% Glass Fiber Reinforced, Heat Stabilized
- Teknor Apex Sinvicomp SPF 8020 Polyvinyl Chloride, Flexible
- A. Schulman POLYBATCH™ Red 5557 Concentrate Based In Polyethylene
- Tisan TISAKRIL® 15% Glass Fiber Reinforced ABS
Copyright © lookpolymers.com All Rights Reserved