SABIC Innovative Plastics LNP THERMOCOMP 9X07430 PBT+PC

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Glass Filled , Polyester, TP , Polybutylene Terephthalate (PBT)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP THERMOCOMP
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP THERMOCOMP 9X07430 PBT+PC.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* THERMOCOMP* 9X07430 is a compoud based on a PBT+PC Blend containing Glass Fiber, Talc. Added features of this material include: Opaque, Weatherable.
Physical Properties Metric English Comments
Density 1.31 g/cc
0.0473 lb/in³
ASTM D792
1.31 g/cc
0.0473 lb/in³
ISO 1183
Moisture Absorption 0.110 %
0.110 %
50% RH, 24 hrs; ASTM D570
0.160 %
0.160 %
23°C / 50% RH; ISO 62
Linear Mold Shrinkage, Flow 0.0051 cm/cm
0.0051 in/in
SABIC Method
0.0050 - 0.0051 cm/cm

@Time 86400 sec
0.0050 - 0.0051 in/in

@Time 24.0 hour
ASTM D955
Linear Mold Shrinkage, Transverse 0.0059 cm/cm
0.0059 in/in
SABIC Method
0.0058 - 0.0059 cm/cm

@Time 86400 sec
0.0058 - 0.0059 in/in

@Time 24.0 hour
ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength at Break 51.0 MPa
7400 psi
Type I, 5 mm/min; ASTM D638
56.0 MPa
8120 psi
5 mm/min; ISO 527
Tensile Strength, Yield 57.0 MPa
8270 psi
Type I, 5 mm/min; ASTM D638
60.0 MPa
8700 psi
5 mm/min; ISO 527
Elongation at Break 4.8 %
4.8 %
Type I, 5 mm/min; ASTM D638
4.9 %
4.9 %
5 mm/min; ISO 527
Elongation at Yield 2.9 %
2.9 %
Type I, 5 mm/min; ASTM D638
3.1 %
3.1 %
5 mm/min; ISO 527
Tensile Modulus 3.16 GPa
458 ksi
1 mm/min; ISO 527
3.30 GPa
479 ksi
50 mm/min; ASTM D638
Flexural Yield Strength 97.0 MPa
14100 psi
2 mm/min; ISO 178
99.0 MPa
14400 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 3.02 GPa
438 ksi
2 mm/min; ISO 178
3.14 GPa
455 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 0.800 J/cm
1.50 ft-lb/in
ASTM D256
Izod Impact, Unnotched 7.15 J/cm
13.4 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 8.00 kJ/m²
3.81 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 47.0 kJ/m²
22.4 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 9.00 J
6.64 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
3.00 J

@Temperature -30.0 °C
2.21 ft-lb

@Temperature -22.0 °F
Instrumented Impact Energy @ peak; ASTM D3763
7.00 J

@Temperature -30.0 °C
5.16 ft-lb

@Temperature -22.0 °F
ASTM D3763
14.0 J

@Temperature 23.0 °C
10.3 ft-lb

@Temperature 73.4 °F
ASTM D3763
Impact Test 7.00 J
5.16 ft-lb
Multiaxial Impact; ISO 6603
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 57.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
31.7 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
CTE, linear, Transverse to Flow 83.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
46.1 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
Deflection Temperature at 1.8 MPa (264 psi) 105 °C
221 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
102 °C

@Thickness 3.20 mm
216 °F

@Thickness 0.126 in
unannealed; ASTM D648