- SABIC Innovative Plastics LNP THERMOCOMP AF004AH ABS
SABIC Innovative Plastics LNP THERMOCOMP AF004AH ABS
| Category | Polymer , Thermoplastic , ABS Polymer |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP AF004AH ABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP THERMOCOMP* AF004AH is a compound based on ABS resin containing 20% Glass Fiber. Added feature of this material is: Healthcare.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.19 g/cc | 0.0430 lb/in³ | ASTM D792 |
| 1.19 g/cc | 0.0430 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.240 % | 0.240 % | 50% RH, 24 hrs; ASTM D570 |
| 0.390 % | 0.390 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm @Time 86400 sec |
0.0020 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0024 cm/cm @Time 86400 sec |
0.0024 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0040 cm/cm @Time 86400 sec |
0.0040 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0040 cm/cm @Time 86400 sec |
0.0040 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 70.0 MPa | 10200 psi | Type I, 5 mm/min; ASTM D638 |
| 81.0 MPa | 11700 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 2.0 % | 2.0 % | 5 mm/min; ISO 527 |
| 2.2 % | 2.2 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 6.00 GPa | 870 ksi | 1 mm/min; ISO 527 |
| 6.17 GPa | 895 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 123 MPa | 17800 psi | ISO 178 |
| 130 MPa | 18900 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 5.86 GPa | 850 ksi | 2 mm/min; ISO 178 |
| 6.15 GPa | 892 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.800 J/cm | 1.50 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 3.95 J/cm | 7.40 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 8.00 kJ/m² | 3.81 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 23.0 kJ/m² | 10.9 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 11.0 J @Temperature 23.0 °C |
8.11 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 3.00 J | 2.21 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 93.0 °C | 199 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 103 °C @Thickness 3.20 mm |
217 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Flammability, UL94 | HB @Thickness 1.50 mm |
HB @Thickness 0.0591 in |
UL 94 |
Users viewing this material also viewed the following:
- Multibase Multi-Pro® 4005 M Polypropylene
- Oceanchem Group Ethylenebistetrabromophthalimide (BT93W)
- Precision Polymer Engineering N70C Nitrile Rubber
- BASF Master Builders Solutions ChemRex® CX-26 Isocyanate-Free Polyurethane-Based Sealant (discontinued **)<
- SK Chemicals SKYTHANE® 198A S series Polyurethane
- ExxonMobil LDPE LD 202.48 Low Density Polyethylene Resin
- Bhansali Engineering Santron IMS 2006 SAN Resin
- SABIC Innovative Plastics PPO 646 PPO (Asia Pacific)
- DuPont Performance Polymers Neoprene SW Polychloroprene Rubber (discontinued **)
Copyright © lookpolymers.com All Rights Reserved