SABIC Innovative Plastics LNP THERMOCOMP AR002XXH ABS

Category Polymer , Thermoplastic , ABS Polymer
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP THERMOCOMP
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP THERMOCOMP AR002XXH ABS.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* THERMOCOMP AR002XXH is a compound based on ABS resin containing 10% Barium Sulfate.
Physical Properties Metric English Comments
Specific Gravity 1.12 g/cc
1.12 g/cc
ASTM D792
Mechanical Properties Metric English Comments
Tensile Strength at Break 40.0 MPa
5800 psi
Type I, 5 mm/min; ASTM D638
Elongation at Break 2.6 %
2.6 %
Type I, 5 mm/min; ASTM D638
Tensile Modulus 2.40 GPa
348 ksi
5 mm/min; ASTM D638
Flexural Strength 68.0 MPa
9860 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 2.56 GPa
371 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 0.840 J/cm
1.57 ft-lb/in
ASTM D256
Izod Impact, Unnotched 2.69 J/cm
5.04 ft-lb/in
ASTM D4812
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 78.0 °C

@Thickness 3.20 mm
 172 °F

@Thickness 0.126 in
 unannealed; ASTM D648