SABIC Innovative Plastics LNP THERMOCOMP DX09402 PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP DX09402 PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* DX09402 is a compound based on Polycarbonate containing Proprietary Filler(s).
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.23 g/cc | 1.23 g/cc | ASTM D792 |
| Density | 1.22 g/cc | 0.0441 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.140 % | 0.140 % | 50% RH, 24 hrs; ASTM D570 |
| 0.180 % | 0.180 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0050 cm/cm @Time 86400 sec |
0.0020 - 0.0050 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0030 - 0.0060 cm/cm @Time 86400 sec |
0.0030 - 0.0060 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 45.0 MPa | 6530 psi | Type I, 5 mm/min; ASTM D638 |
| 47.0 MPa | 6820 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 55.0 MPa | 7980 psi | 5 mm/min; ISO 527 |
| 56.0 MPa | 8120 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 21.3 % | 21.3 % | 5 mm/min; ISO 527 |
| 36.8 % | 36.8 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 5.1 % | 5.1 % | 5 mm/min; ISO 527 |
| 5.3 % | 5.3 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 2.97 GPa | 431 ksi | 50 mm/min; ASTM D638 |
| 2.99 GPa | 434 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 81.0 MPa | 11700 psi | ISO 178 |
| Flexural Modulus | 2.64 GPa | 383 ksi | 2 mm/min; ISO 178 |
| 2.81 GPa | 408 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 4.31 J/cm | 8.07 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 22.6 J/cm | 42.3 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 29.0 kJ/m² | 13.8 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 201 kJ/m² | 95.6 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 41.0 J @Temperature 23.0 °C |
30.2 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 43.0 J | 31.7 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 54.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
30.0 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 78.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
43.3 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 136 °C | 277 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 138 °C @Thickness 3.20 mm |
280 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 125 °C | 257 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 129 °C @Thickness 3.20 mm |
264 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Nye Lubricants 358PC (RL) Synthetic Oil
- Nye Lubricants 719A (RL) Rheolube Grease
- Ohio Carbon Blank OCB UT-2E Mechanical Grade Graphite
- Quadrant Plastic Composites GMTex® Glass-Mat-Reinforced Thermoplastic
- Gwent Electronic Materials D2020823D2 Polymer Dielectric
- Karina E 836-10/176-CRA White PVC Compound
- SABIC Innovative Plastics LNP LUBRICOMP KL001 Acetal Copolymer
- Chicago Extruded Metals UNS C36000 Copper-Zinc-Lead Alloy
- Dow 4010 Low Density Polyethylene (LDPE)
Copyright © lookpolymers.com All Rights Reserved