SABIC Innovative Plastics LNP THERMOCOMP EX06430H PEI
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP EX06430H PEI.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* EX06430H is a compound based on Polyetherimide resin containing Proprietary Filler(s). Added feature of this grade is: Healthcare.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.34 - 1.40 g/cc | 0.0484 - 0.0506 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0070 cm/cm @Time 86400 sec |
0.0070 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm @Time 86400 sec |
0.0080 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 90.0 MPa | 13100 psi | ASTM D638 |
| 90.0 MPa | 13100 psi | ISO 527 | |
| Tensile Strength, Yield | 106 MPa | 15400 psi | ISO 527 |
| 110 MPa | 16000 psi | ASTM D638 | |
| Elongation at Break | 10.8 % | 10.8 % | ISO 527 |
| 13.5 % | 13.5 % | ASTM D638 | |
| Elongation at Yield | 6.0 % | 6.0 % | ISO 527 |
| 6.7 % | 6.7 % | ASTM D638 | |
| Tensile Modulus | 3.50 GPa | 508 ksi | 1 mm/min; ISO 527 |
| 3.66 GPa | 531 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 133 MPa | 19300 psi | ISO 178 |
| Flexural Modulus | 3.50 GPa | 508 ksi | ISO 178 |
| 3.66 GPa | 531 ksi | ASTM D790 | |
| Izod Impact, Notched | 0.480 J/cm | 0.899 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 13.83 J/cm | 25.91 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 73.0 kJ/m² | 34.7 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 10.0 J | 7.38 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 194 °C | 381 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 195 °C @Thickness 3.20 mm |
383 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Multibase Multi-Pro® 2518 TU Polypropylene
- MV Labs HO500 HoF3 Holmium fluoride
- 3M Dyneon™ TF 5032 PTFE Dispersion (discontinued **)
- Haynes 556® alloy, bar, after 1000 hours at 760°C (1400°F)
- SABIC Innovative Plastics NORYL WCD801A PPE-TPE (Asia Pacific)
- SABIC Innovative Plastics PC2200R PC (Europe-Africa-Middle East)
- Seals Eastern 7352D Nano-PTFE Filled Fluoroelastomer
- Vyncolit 4451 XB Novolac Phenolic
- Wingate Alloys Winco Heat Treated, High Tensile Alloy Steel for Maintenance and Machine Repair
- ExxonMobil HDPE HD 8760.29 High Density Polyethylene Resin
Copyright © lookpolymers.com All Rights Reserved