SABIC Innovative Plastics LNP THERMOCOMP J1000ER PES (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Polyethersulfone (PES)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP THERMOCOMP
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP THERMOCOMP J1000ER PES (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* THERMOCOMP* J1000ER is a compound based on Polyethersulfone resin. Added features include : Easy Molding, Mold Release
Physical Properties Metric English Comments
Density 1.38 g/cc
0.0499 lb/in³
ISO 1183
Water Absorption 1.7 %

@Time 86400 sec
1.7 %

@Time 24.0 hour
ISO 62-1
Linear Mold Shrinkage, Flow 0.0090 cm/cm
0.0090 in/in
SABIC Method
Mechanical Properties Metric English Comments
Tensile Strength at Break 77.0 MPa
11200 psi
50 mm/min; ISO 527
Tensile Strength, Yield 88.0 MPa
12800 psi
50 mm/min; ISO 527
Elongation at Yield 6.6 %
6.6 %
50 mm/min; ISO 527
Tensile Modulus 2.70 GPa
392 ksi
1 mm/min; ISO 527
Flexural Yield Strength 129 MPa
18700 psi
2 mm/min; ISO 178
Flexural Modulus 2.60 GPa
377 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 6.00 kJ/m²
2.86 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) NB
NB
80*10*4; ISO 180/1U
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 200 °C
392 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af