SABIC Innovative Plastics LNP THERMOCOMP KF006XXC Acetal Copolymer (Asia Pacific)

Category Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, 30% Glass Fiber Reinforced
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP THERMOCOMP
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP THERMOCOMP KF006XXC Acetal Copolymer (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Thermocomp* KF006XXC is a compound based on Acetal Copolymer resin containing Glass Fiber.
Physical Properties Metric English Comments
Density 1.64 g/cc
0.0592 lb/in³
ASTM D792
1.64 g/cc
0.0592 lb/in³
ISO 1183
Moisture Absorption 0.200 %
0.200 %
50% RH, 24 hrs; ASTM D570
Linear Mold Shrinkage, Flow 0.0049 cm/cm

@Time 86400 sec
 0.0049 in/in

@Time 24.0 hour
 ISO 294
0.0050 cm/cm

@Time 86400 sec
 0.0050 in/in

@Time 24.0 hour
 ASTM D955
Linear Mold Shrinkage, Transverse 0.016 cm/cm

@Time 86400 sec
 0.016 in/in

@Time 24.0 hour
 ASTM D955
0.016 cm/cm

@Time 86400 sec
 0.016 in/in

@Time 24.0 hour
 ISO 294
Mechanical Properties Metric English Comments
Tensile Strength at Break 115 MPa
16700 psi
ASTM D638
121 MPa
17500 psi
ISO 527
Tensile Strength, Yield 115 MPa
16700 psi
ASTM D638
121 MPa
17500 psi
ISO 527
Elongation at Break 2.0 %
2.0 %
ASTM D638
2.1 %
2.1 %
ISO 527
Elongation at Yield 2.0 %
2.0 %
ASTM D638
2.1 %
2.1 %
ISO 527
Tensile Modulus 10.35 GPa
1501 ksi
1 mm/min; ISO 527
11.03 GPa
1600 ksi
50 mm/min; ASTM D638
Flexural Strength 172 MPa
24900 psi
ASTM D790
176 MPa
25500 psi
ISO 178
Flexural Modulus 9.00 GPa
1310 ksi
ISO 178
9.65 GPa
1400 ksi
ASTM D790
Izod Impact, Notched 0.530 J/cm
0.993 ft-lb/in
ASTM D256
Izod Impact, Unnotched 6.40 J/cm
12.0 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 7.00 kJ/m²
3.33 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 41.0 kJ/m²
19.5 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 8.00 J
5.90 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Impact Test 3.00 J
2.21 ft-lb
Multiaxial Impact; ISO 6603
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 82.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 45.6 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
82.8 µm/m-°C

@Temperature -40.0 - 40.0 °C
 46.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
CTE, linear, Transverse to Flow 36.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 20.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
37.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 20.6 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 164 °C
327 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
162 °C

@Thickness 3.20 mm
 324 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 161 °C
322 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
162 °C

@Thickness 3.20 mm
 324 °F

@Thickness 0.126 in
 unannealed; ASTM D648