SABIC Innovative Plastics LNP THERMOCOMP KFZ24XXP Acetal Copoly

Category Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, 30% Glass Fiber Reinforced
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP THERMOCOMP
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP THERMOCOMP KFZ24XXP Acetal Copoly.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* THERMOCOMP* KFZ24XXP is a compound based on Acetal Copolymer resin containing 20% Glass Fiber, 10% Milled Glass. Added features of this material include: Low Warpage, Chemically Coupled, Internally Lubricated.
Physical Properties Metric English Comments
Density 1.64 g/cc
0.0592 lb/in³
ASTM D792
1.64 g/cc
0.0592 lb/in³
ISO 1183
Moisture Absorption 0.100 %
0.100 %
50% RH, 24 hrs; ASTM D570
Linear Mold Shrinkage, Flow 0.0066 cm/cm

@Time 86400 sec
 0.0066 in/in

@Time 24.0 hour
 ISO 294
0.0070 cm/cm

@Time 86400 sec
 0.0070 in/in

@Time 24.0 hour
 ASTM D955
Linear Mold Shrinkage, Transverse 0.013 cm/cm

@Time 86400 sec
 0.013 in/in

@Time 24.0 hour
 ASTM D955
0.013 cm/cm

@Time 86400 sec
 0.013 in/in

@Time 24.0 hour
 ISO 294
Mechanical Properties Metric English Comments
Tensile Strength at Break 105 MPa
15200 psi
ASTM D638
109 MPa
15800 psi
ISO 527
Elongation at Break 2.5 %
2.5 %
ASTM D638
2.6 %
2.6 %
ISO 527
Tensile Modulus 8.54 GPa
1240 ksi
50 mm/min; ASTM D638
8.90 GPa
1290 ksi
1 mm/min; ISO 527
Flexural Strength 165 MPa
23900 psi
ASTM D790
171 MPa
24800 psi
ISO 178
Flexural Modulus 7.58 GPa
1100 ksi
ASTM D790
9.40 GPa
1360 ksi
ISO 178
Izod Impact, Notched 0.640 J/cm
1.20 ft-lb/in
ASTM D256
Izod Impact, Unnotched 5.34 J/cm
10.0 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 6.00 kJ/m²
2.86 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 36.0 kJ/m²
17.1 ft-lb/in²
80*10*4; ISO 180/1U
Dart Drop, Total Energy 10.0 J
7.38 ft-lb
Instrumented Impact Energy @ peak; ASTM D3763
Impact Test 2.00 J
1.48 ft-lb
Multiaxial Impact; ISO 6603
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 163 °C

@Thickness 3.20 mm
 325 °F

@Thickness 0.126 in
 unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 160 °C
320 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
161 °C

@Thickness 3.20 mm
 322 °F

@Thickness 0.126 in
 unannealed; ASTM D648