SABIC Innovative Plastics LNP THERMOCOMP Noryl_PCN2910 PPE+PS (Asia Pacific)

Category Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP THERMOCOMP
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP THERMOCOMP Noryl_PCN2910 PPE+PS (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
35% Glass/Mica filled. High modulus and tight tolerance molding for the chassis market.
Physical Properties Metric English Comments
Specific Gravity 1.38 g/cc
1.38 g/cc
ASTM D792
Linear Mold Shrinkage, Flow 0.0010 - 0.0030 cm/cm

@Thickness 3.20 mm
0.0010 - 0.0030 in/in

@Thickness 0.126 in
SABIC Method
Linear Mold Shrinkage, Transverse 0.0040 - 0.0060 cm/cm

@Thickness 3.20 mm
0.0040 - 0.0060 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 10 g/10 min

@Load 5.00 kg,
Temperature 300 °C
10 g/10 min

@Load 11.0 lb,
Temperature 572 °F
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 106 MPa
15400 psi
5 mm/min; ISO 527
122 MPa
17700 psi
Type I, 5 mm/min; ASTM D638
Tensile Strength, Yield 106 MPa
15400 psi
5 mm/min; ISO 527
122 MPa
17700 psi
Type I, 5 mm/min; ASTM D638
Elongation at Break 1.3 %
1.3 %
5 mm/min; ISO 527
1.5 %
1.5 %
Type I, 5 mm/min; ASTM D638
Elongation at Yield 1.3 %
1.3 %
5 mm/min; ISO 527
1.5 %
1.5 %
Type I, 5 mm/min; ASTM D638
Tensile Modulus 10.6 GPa
1540 ksi
1 mm/min; ISO 527
11.37 GPa
1649 ksi
5 mm/min; ASTM D638
Flexural Strength 151 MPa
21900 psi
2.6 mm/min, 100 mm span; ASTM D790
160 MPa
23200 psi
2 mm/min; ISO 178
165 MPa
23900 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Yield Strength 160 MPa
23200 psi
2 mm/min; ISO 178
Flexural Modulus 8.75 GPa
1270 ksi
2.6 mm/min, 100 mm span; ASTM D790
9.13 GPa
1320 ksi
2 mm/min; ISO 178
9.79 GPa
1420 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 0.580 J/cm
1.09 ft-lb/in
ASTM D256
Izod Impact, Unnotched 3.31 J/cm
6.20 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 5.00 kJ/m²
2.38 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 14.0 kJ/m²
6.66 ft-lb/in²
80*10*4; ISO 180/1U
Charpy Impact Unnotched 2.00 J/cm²
9.52 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eU
Charpy Impact, Notched 0.400 J/cm²
1.90 ft-lb/in²
ISO 179/2C
Dart Drop, Total Energy 7.00 J

@Temperature 23.0 °C
5.16 ft-lb

@Temperature 73.4 °F
ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 21.6 µm/m-°C

@Temperature -40.0 - 40.0 °C
12.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
CTE, linear, Transverse to Flow 46.8 µm/m-°C

@Temperature -40.0 - 40.0 °C
26.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
Deflection Temperature at 0.46 MPa (66 psi) 129 °C

@Thickness 3.20 mm
264 °F

@Thickness 0.126 in
unannealed; ASTM D648
129 °C

@Thickness 6.40 mm
264 °F

@Thickness 0.252 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 129 °C
264 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
123 °C

@Thickness 3.20 mm
253 °F

@Thickness 0.126 in
unannealed; ASTM D648
126 °C

@Thickness 6.40 mm
259 °F

@Thickness 0.252 in
unannealed; ASTM D648
Vicat Softening Point 140 °C
284 °F
Rate B/50; ASTM D1525
UL RTI, Electrical 65.0 °C
149 °F
UL 746B
UL RTI, Mechanical with Impact 65.0 °C
149 °F
UL 746B
UL RTI, Mechanical without Impact 65.0 °C
149 °F
UL 746B
Flammability, UL94 V-1

@Thickness 1.49 mm
V-1

@Thickness 0.0587 in
UL 94
V-0

@Thickness 2.99 mm
V-0

@Thickness 0.118 in
UL 94
5VB

@Thickness 2.28 mm
5VB

@Thickness 0.0898 in
UL 94