SABIC Innovative Plastics LNP THERMOCOMP PDXE98480 PEI
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP PDXE98480 PEI.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Thermocomp* PDXE98480 is a compound based on Polyetherimide with Proprietary Fillers. Added feature of this grade: Reinforced.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.60 g/cc | 1.60 g/cc | ASTM D792 |
| Density | 1.60 g/cc | 0.0578 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.120 % | 0.120 % | 50% RH, 24 hrs; ASTM D570 |
| 0.170 % | 0.170 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0040 cm/cm @Time 86400 sec |
0.0020 - 0.0040 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0040 - 0.0060 cm/cm @Time 86400 sec |
0.0040 - 0.0060 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 162 MPa | 23500 psi | 5 mm/min; ISO 527 |
| 180 MPa | 26100 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 1.5 % | 1.5 % | 5 mm/min; ISO 527 |
| 1.7 % | 1.7 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 14.22 GPa | 2062 ksi | 1 mm/min; ISO 527 |
| 15.1 GPa | 2190 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 243 MPa | 35200 psi | ISO 178 |
| 254 MPa | 36800 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 12.79 GPa | 1855 ksi | 2 mm/min; ISO 178 |
| 13.4 GPa | 1940 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.920 J/cm | 1.72 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 5.00 J/cm | 9.37 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 8.00 kJ/m² | 3.81 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 33.0 kJ/m² | 15.7 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 12.0 J @Temperature 23.0 °C |
8.85 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 4.00 J | 2.95 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 29.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
16.1 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 92.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
51.1 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 213 °C | 415 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 213 °C @Thickness 3.20 mm |
415 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 208 °C | 406 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 208 °C @Thickness 3.20 mm |
406 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Cycolac® FR30U ABS (Asia Pacific)
- LATI Kelon® B H CER/30 PA 6, 30% Mineral Reinforced, Heat Stabilized
- Haynes Ultimet® alloy, 12.7 mm (1/2 in.) thick plate, GTAW weld
- SPS Guang Zhou SAMATâ„¢ 5000AC Flame-retarded Polypropylene
- Borealis Xmod™ K65G2 20% Glass Fiber Reinforced Polypropylene Compound
- EMS-Griltech Griltex® D 1564A Heat Stabilized Copolyamide Hotmelt Adhesive (Technical Applications)
- Ensinger Tecapeek® XP-94 Compression Molded PEEK Compound, 20% Fiberglass
- Latrobe DuraTech™ A11 Powder Metal Tool Steel (AISI A11)
Copyright © lookpolymers.com All Rights Reserved