SABIC Innovative Plastics LNP THERMOCOMP PH0800A PA 6
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP PH0800A PA 6.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* PH0800A is a compound based on Nylon 6 resin. Added feature of this material is: High Specific Gravity.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 7.81 g/cc | 7.81 g/cc | ASTM D792 |
| Density | 7.79 g/cc | 0.281 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.110 % | 0.110 % | 50% RH, 24 hrs; ASTM D570 |
| 0.180 % | 0.180 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | >= 0.020 cm/cm @Time 86400 sec |
>= 0.020 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.030 cm/cm @Time 86400 sec |
0.010 - 0.030 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 54.0 MPa | 7830 psi | Type I, 5 mm/min; ASTM D638 |
| 54.0 MPa | 7830 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 54.0 MPa | 7830 psi | Type I, 5 mm/min; ASTM D638 |
| 54.0 MPa | 7830 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 0.80 % | 0.80 % | 5 mm/min; ISO 527 |
| 1.0 % | 1.0 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 0.80 % | 0.80 % | 5 mm/min; ISO 527 |
| 1.0 % | 1.0 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 8.68 GPa | 1260 ksi | 1 mm/min; ISO 527 |
| 9.06 GPa | 1310 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 81.0 MPa | 11700 psi | ISO 178 |
| 81.0 MPa | 11700 psi | 2 mm/min; ISO 178 | |
| 86.0 MPa | 12500 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 5.71 GPa | 828 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 8.34 GPa | 1210 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.710 J/cm | 1.33 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 2.20 J/cm | 4.12 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² | 1.90 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 16.0 kJ/m² | 7.61 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 8.00 J @Temperature 23.0 °C |
5.90 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 52.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
28.9 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 43.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
23.9 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 192 °C | 378 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 193 °C @Thickness 3.20 mm |
379 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 132 °C | 270 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 145 °C @Thickness 3.20 mm |
293 °F @Thickness 0.126 in |
unannealed; ASTM D648 |