SABIC Innovative Plastics LNP THERMOCOMP RF00C PA 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP RF00C PA 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP THERMOCOMP* RF00C is a compound based on Nylon 66 resin containing 60% Glass Fiber.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.68 g/cc | 1.68 g/cc | ASTM D792 |
| Density | 1.68 g/cc | 0.0607 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.420 % | 0.420 % | 50% RH, 24 hrs; ASTM D570 |
| 0.600 % | 0.600 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0050 cm/cm @Time 86400 sec |
0.0030 - 0.0050 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.030 cm/cm @Time 86400 sec |
0.010 - 0.030 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 247 MPa | 35800 psi | Type I, 5 mm/min; ASTM D638 |
| 250 MPa | 36300 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 2.1 % | 2.1 % | Type I, 5 mm/min; ASTM D638 |
| 2.2 % | 2.2 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 20.36 GPa | 2953 ksi | 1 mm/min; ISO 527 |
| 21.12 GPa | 3063 ksi | 5 mm/min; ASTM D638 | |
| Flexural Strength | 377 MPa | 54700 psi | ISO 178 |
| 383 MPa | 55500 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Yield Strength | 384 MPa | 55700 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 18.3 GPa | 2650 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 18.48 GPa | 2680 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 1.59 J/cm | 2.98 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 13.4 J/cm | 25.1 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 16.0 kJ/m² | 7.61 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 76.0 kJ/m² | 36.2 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 12.0 J @Temperature 23.0 °C |
8.85 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 5.00 J | 3.69 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 40.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
22.2 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 21.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
11.7 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 260 °C | 500 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 260 °C @Thickness 3.20 mm |
500 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 254 °C | 489 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 255 °C @Thickness 3.20 mm |
491 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- MV Labs SC700 Sc(NO3)3·5H2O Scandium nitrate hydrate
- Kazanorgsintez 10803-020 High Pressure Polyethylene
- Lehmann & Voss LUVOCOM® 20-7908 Polyphthalamide, with glass fiber and carbon fiber
- Sylvin Technologies 9980-80 Natural PVC Molding Compound
- Chase Plastics CP Pryme® AC300 Acetal Copolymer, Recycled Content
- DuPont Performance Polymers Crastin® CE2061 BK560 PBT
- BASF PolyTHF® 1000 Polyether
- Asahi Glass Fluon® CD123 PTFE Coagulated Dispersion Powder
- Beijing Evergrow Resources ER-21 UHMW PE Bulletproof Plate
- Abatron 85062 A/B Filled Potting Compound (discontinued **)
Copyright © lookpolymers.com All Rights Reserved