SABIC Innovative Plastics LNP THERMOCOMP RFB53XXZ PA 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP RFB53XXZ PA 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* RFB53XXZ is a compound based on Nylon 66 resin containing 15% Glass Fiber, 25% Glass Bead.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.46 g/cc | 1.46 g/cc | ASTM D792 |
| Density | 1.46 g/cc | 0.0527 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.630 % | 0.630 % | 50% RH, 24 hrs; ASTM D570 |
| 0.950 % | 0.950 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0070 cm/cm @Time 86400 sec |
0.0040 - 0.0070 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0090 - 0.020 cm/cm @Time 86400 sec |
0.0090 - 0.020 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 115 MPa | 16700 psi | Type I, 5 mm/min; ASTM D638 |
| 124 MPa | 18000 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 124 MPa | 18000 psi | Type I, 5 mm/min; ASTM D638 |
| 125 MPa | 18100 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 2.7 % | 2.7 % | Type I, 5 mm/min; ASTM D638 |
| 2.7 % | 2.7 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 2.6 % | 2.6 % | Type I, 5 mm/min; ASTM D638 |
| 2.6 % | 2.6 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 8.10 GPa | 1170 ksi | 1 mm/min; ISO 527 |
| 8.45 GPa | 1230 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 183 MPa | 26500 psi | ISO 178 |
| 186 MPa | 27000 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Yield Strength | 186 MPa | 27000 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 7.04 GPa | 1020 ksi | 2 mm/min; ISO 178 |
| 7.32 GPa | 1060 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.370 J/cm | 0.693 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 4.96 J/cm | 9.29 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 4.00 kJ/m² | 1.90 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 33.0 kJ/m² | 15.7 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 7.00 J @Temperature 23.0 °C |
5.16 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 40.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
22.2 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 84.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
46.7 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 253 °C | 487 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 256 °C @Thickness 3.20 mm |
493 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 234 °C | 453 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 241 °C @Thickness 3.20 mm |
466 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- PolyOne Maxxam™ NT-818.G002-1000 Polypropylene, Unspecified (PP, Unspecified)
- Kureha KF Polymer 850 PVDF Homopolymer
- Lehmann & Voss LUVOCOM® 1105/GF/30/BK-1 PEEK, with glass fiber
- Solvay ALKAMULS® S 20 Surfactant
- Sumitomo Bakelite North America RX® 431 Cellulose Reinforced Phenolic Novolac
- Epoxyset Epoxibond EB-107LP-2 Unfilled Epoxy Adhesive
- Eurotec® Tecomid® NA40 CR20 BK111 PA6.6, 20% carbon fiber reinforced, black
- Akzo Nobel Expancel® 091 DU 80 Dry unexpanded microspheres
- Haynes 556® alloy, 40% cold reduction, 1065°C anneal for 5 minutes
Copyright © lookpolymers.com All Rights Reserved