- SABIC Innovative Plastics LNP Thermocomp 5C003
SABIC Innovative Plastics LNP Thermocomp 5C003
| Category | Polymer , Thermoplastic , Fluoropolymer , PVDF , Polyvinylidinefluoride (PVDF), with Carbon Fiber |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Thermocomp 5C003.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP THERMOCOMP* 5C003 is a compound based on Polyvinylidene Fluoride resin containing Carbon Fiber. Added features of this material include: Electrically Conductive. Also known as THERMOCOMP* FP-VC-1003This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.76 g/cc | 0.0636 lb/in³ | ISO 1183 |
| 1.769 g/cc | 0.06391 lb/in³ | ASTM D 792 | |
| Moisture Absorption at Equilibrium | 0.040 % | 0.040 % | 23°C / 50% RH; ISO 62 |
| 0.030 % @Time 86400 sec |
0.030 % @Time 24.0 hour |
50% RH; ASTM D 570 | |
| Linear Mold Shrinkage, Flow | 0.0036 cm/cm @Time 86400 sec |
0.0036 in/in @Time 24.0 hour |
ISO 294 |
| 0.0030 - 0.0050 cm/cm @Time 86400 sec |
0.0030 - 0.0050 in/in @Time 24.0 hour |
ASTM D 955 | |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.013 cm/cm @Time 86400 sec |
0.010 - 0.013 in/in @Time 24.0 hour |
ASTM D 955 |
| 0.0116 cm/cm @Time 86400 sec |
0.0116 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 67.0 MPa | 9720 psi | ISO 527 |
| 78.0 MPa | 11300 psi | ASTM D 638 | |
| Elongation at Break | 0.60 % | 0.60 % | ISO 527 |
| 0.80 % | 0.80 % | ASTM D 638 | |
| Tensile Modulus | 14.27 GPa | 2070 ksi | 50 mm/min; ASTM D 638 |
| 14.5 GPa | 2100 ksi | 1 mm/min; ISO 527 | |
| Flexural Strength | 127 MPa | 18400 psi | ASTM D 790 |
| 147 MPa | 21300 psi | ISO 178 | |
| Flexural Modulus | 11.79 GPa | 1710 ksi | ASTM D 790 |
| 20.92 GPa | 3034 ksi | ISO 178 | |
| Izod Impact, Notched | 0.580 J/cm @Temperature 23.0 °C |
1.09 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 2.02 J/cm @Temperature 23.0 °C |
3.78 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² @Temperature 23.0 °C |
2.86 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 14.0 kJ/m² @Temperature 23.0 °C |
6.66 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Impact Test | 3.00 J | 2.21 ft-lb | Multiaxial Impact; ISO 6603 |
| 11.0 J @Temperature 23.0 °C |
8.11 ft-lb @Temperature 73.4 °F |
Instrumented Impact Energy @ peak; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 31.3 µm/m-°C @Temperature -40.0 - 40.0 °C |
17.4 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 31.3 µm/m-°C @Temperature -40.0 - 40.0 °C |
17.4 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 86.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
47.9 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 86.2 µm/m-°C @Temperature -40.0 - 40.0 °C |
47.9 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 165 °C | 329 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 165 °C @Thickness 3.20 mm |
329 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 156 °C | 313 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 159 °C @Thickness 3.20 mm |
318 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |