SABIC Innovative Plastics LNP Thermocomp 5X06476 FP-V (PVDF)
| Category | Polymer , Thermoplastic , Fluoropolymer , PVDF |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Thermocomp 5X06476 FP-V (PVDF).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* FP-VM-3830 is a compound based on Polyvinylidine Fluoride (PVDF) containing Mineral.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.89 g/cc | 1.89 g/cc | ASTM D 792 |
| Density | 1.89 g/cc | 0.0683 lb/in³ | ASTM D 792 |
| Moisture Absorption at Equilibrium | 0.010 % | 0.010 % | 23°C / 50% RH; ISO 62 |
| 0.020 % @Time 86400 sec |
0.020 % @Time 24.0 hour |
50% RH; ASTM D 570 | |
| Linear Mold Shrinkage, Flow | 0.010 - 0.030 cm/cm @Time 86400 sec |
0.010 - 0.030 in/in @Time 24.0 hour |
ASTM D 955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.030 cm/cm @Time 86400 sec |
0.010 - 0.030 in/in @Time 24.0 hour |
ASTM D 955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 35.0 MPa | 5080 psi | 5 mm/min; ISO 527 |
| 37.0 MPa | 5370 psi | Type I, 5 mm/min; ASTM D 638 | |
| Tensile Strength, Yield | 37.0 MPa | 5370 psi | 5 mm/min; ISO 527 |
| 39.0 MPa | 5660 psi | Type I, 5 mm/min; ASTM D 638 | |
| Elongation at Break | 19 % | 19 % | Type I, 5 mm/min; ASTM D 638 |
| 20.9 % | 20.9 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 7.4 % | 7.4 % | Type I, 5 mm/min; ASTM D 638 |
| 7.4 % | 7.4 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 2.36 GPa | 342 ksi | 1 mm/min; ISO 527 |
| 2.54 GPa | 368 ksi | 50 mm/min; ASTM D 638 | |
| Flexural Strength | 53.0 MPa | 7690 psi | ISO 178 |
| Flexural Modulus | 2.20 GPa | 319 ksi | 2 mm/min; ISO 178 |
| 2.32 GPa | 336 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Izod Impact, Notched | 0.420 J/cm @Temperature 23.0 °C |
0.787 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 4.73 J/cm @Temperature 23.0 °C |
8.86 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² @Temperature 23.0 °C |
2.86 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 30.0 kJ/m² @Temperature 23.0 °C |
14.3 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Impact Test | 1.00 J | 0.738 ft-lb | Multiaxial Impact; ISO 6603 |
| 5.00 J @Temperature 23.0 °C |
3.69 ft-lb @Temperature 73.4 °F |
Instrumented Impact Total Energy; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 122 µm/m-°C @Temperature -30.0 - 30.0 °C |
67.8 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D 696 |
| CTE, linear, Transverse to Flow | 146 µm/m-°C @Temperature -30.0 - 30.0 °C |
81.1 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D 696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 137 °C | 279 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 143 °C @Thickness 3.20 mm |
289 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C | 185 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 99.0 °C @Thickness 3.20 mm |
210 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |