SABIC Innovative Plastics LNP Thermocomp FF008L PE
| Category | Polymer , Thermoplastic , Polyethylene (PE) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Thermocomp FF008L PE.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Thermocomp* FF008L is a compounding based on Polyethylene containing glass fiber. Added characteristics include Low Extractible.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.27 g/cc | 1.27 g/cc | ASTM D 792 |
| Density | 1.27 g/cc | 0.0459 lb/in³ | ASTM D 792 |
| Moisture Absorption at Equilibrium | 0.030 % | 0.030 % | 23°C / 50% RH; ISO 62 |
| 0.030 % @Time 86400 sec |
0.030 % @Time 24.0 hour |
50% RH; ASTM D 570 | |
| Linear Mold Shrinkage, Flow | 0.0090 - 0.020 cm/cm @Time 86400 sec |
0.0090 - 0.020 in/in @Time 24.0 hour |
ASTM D 955 |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.030 cm/cm @Time 86400 sec |
0.010 - 0.030 in/in @Time 24.0 hour |
ASTM D 955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 33.0 MPa | 4790 psi | Type I, 5 mm/min; ASTM D 638 |
| 34.0 MPa | 4930 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 34.0 MPa | 4930 psi | 5 mm/min; ISO 527 |
| 36.0 MPa | 5220 psi | Type I, 5 mm/min; ASTM D 638 | |
| Elongation at Break | 0.70 % | 0.70 % | 5 mm/min; ISO 527 |
| 0.80 % | 0.80 % | Type I, 5 mm/min; ASTM D 638 | |
| Elongation at Yield | 0.70 % | 0.70 % | 5 mm/min; ISO 527 |
| 0.70 % | 0.70 % | Type I, 5 mm/min; ASTM D 638 | |
| Tensile Modulus | 6.49 GPa | 941 ksi | 1 mm/min; ISO 527 |
| 8.47 GPa | 1230 ksi | 50 mm/min; ASTM D 638 | |
| Flexural Strength | 47.0 MPa | 6820 psi | ISO 178 |
| 61.0 MPa | 8850 psi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Flexural Yield Strength | 69.0 MPa | 10000 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Flexural Modulus | 2.75 GPa | 399 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| 6.25 GPa | 906 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.450 J/cm @Temperature 23.0 °C |
0.843 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 1.37 J/cm @Temperature 23.0 °C |
2.57 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 3.00 kJ/m² @Temperature 23.0 °C |
1.43 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 7.00 kJ/m² @Temperature 23.0 °C |
3.33 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| 8.00 J @Temperature 23.0 °C |
5.90 ft-lb @Temperature 73.4 °F |
Instrumented Impact Total Energy; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 37.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
20.6 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D 696 |
| CTE, linear, Transverse to Flow | 65.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
36.1 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D 696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 127 °C | 261 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 127 °C @Thickness 3.20 mm |
261 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 96.0 °C | 205 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 97.0 °C @Thickness 3.20 mm |
207 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |