SABIC Innovative Plastics LNP Thermocomp LFZ42XXC PEEK

Category Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP THERMOCOMP
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP Thermocomp LFZ42XXC PEEK.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP THERMOCOMP* LFZ42XXC is a compound based on Polyetheretherketone resin containing Glass Fiber, Milled Glass. Added features of this material include: Low Warpage.This data was supplied by SABIC-IP for the Americas region.
Physical Properties Metric English Comments
Density 1.52 g/cc
0.0549 lb/in³
ISO 1183
1.53 g/cc
0.0553 lb/in³
ASTM D 792
Moisture Absorption at Equilibrium 0.080 %
0.080 %
23°C / 50% RH; ISO 62
0.060 %

@Time 86400 sec
0.060 %

@Time 24.0 hour
50% RH; ASTM D 570
Linear Mold Shrinkage, Flow 0.0040 - 0.0070 cm/cm

@Time 86400 sec
0.0040 - 0.0070 in/in

@Time 24.0 hour
ASTM D 955
Linear Mold Shrinkage, Transverse 0.0060 - 0.0090 cm/cm

@Time 86400 sec
0.0060 - 0.0090 in/in

@Time 24.0 hour
ASTM D 955
Mechanical Properties Metric English Comments
Tensile Strength at Break 110 MPa
16000 psi
5 mm/min; ISO 527
111 MPa
16100 psi
Type I, 5 mm/min; ASTM D 638
Tensile Strength, Yield 111 MPa
16100 psi
5 mm/min; ISO 527
112 MPa
16200 psi
Type I, 5 mm/min; ASTM D 638
Elongation at Break 3.0 %
3.0 %
5 mm/min; ISO 527
3.1 %
3.1 %
Type I, 5 mm/min; ASTM D 638
Elongation at Yield 2.8 %
2.8 %
5 mm/min; ISO 527
2.9 %
2.9 %
Type I, 5 mm/min; ASTM D 638
Tensile Modulus 7.11 GPa
1030 ksi
50 mm/min; ASTM D 638
7.72 GPa
1120 ksi
1 mm/min; ISO 527
Flexural Strength 178 MPa
25800 psi
1.3 mm/min, 50 mm span; ASTM D 790
Flexural Yield Strength 179 MPa
26000 psi
1.3 mm/min, 50 mm span; ASTM D 790
Flexural Modulus 6.85 GPa
994 ksi
2 mm/min; ISO 178
7.22 GPa
1050 ksi
1.3 mm/min, 50 mm span; ASTM D 790
Izod Impact, Notched 0.550 J/cm

@Temperature 23.0 °C
1.03 ft-lb/in

@Temperature 73.4 °F
ASTM D 256
Izod Impact, Unnotched 7.05 J/cm

@Temperature 23.0 °C
13.2 ft-lb/in

@Temperature 73.4 °F
ASTM D 4812
Izod Impact, Notched (ISO) 5.00 kJ/m²

@Temperature 23.0 °C
2.38 ft-lb/in²

@Temperature 73.4 °F
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 40.0 kJ/m²

@Temperature 23.0 °C
19.0 ft-lb/in²

@Temperature 73.4 °F
80*10*4; ISO 180/1U
Impact Test 4.00 J
2.95 ft-lb
Multiaxial Impact; ISO 6603
8.00 J

@Temperature 23.0 °C
5.90 ft-lb

@Temperature 73.4 °F
Instrumented Impact Total Energy; ASTM D 3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 30.6 µm/m-°C

@Temperature -30.0 - 30.0 °C
17.0 µin/in-°F

@Temperature -22.0 - 86.0 °F
ASTM D 696
CTE, linear, Transverse to Flow 36.5 µm/m-°C

@Temperature -30.0 - 30.0 °C
20.3 µin/in-°F

@Temperature -22.0 - 86.0 °F
ASTM D 696
Deflection Temperature at 0.46 MPa (66 psi) 315 °C
599 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
Deflection Temperature at 1.8 MPa (264 psi) 198 °C
388 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
156 °C

@Thickness 3.20 mm
313 °F

@Thickness 0.126 in
unannealed; ASTM D 648