- SABIC Innovative Plastics LNP Thermocomp OK006 PPS - Linear
SABIC Innovative Plastics LNP Thermocomp OK006 PPS - Linear
| Category | Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Thermocomp OK006 PPS - Linear.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Thermocomp* OK006 is based on a Linear Polyphenylene Sulfide (PPS) containing Talc.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.59 g/cc | 0.0574 lb/in³ | ASTM D 792 |
| 1.59 g/cc | 0.0574 lb/in³ | ISO 1183 | |
| Moisture Absorption at Equilibrium | 0.030 % | 0.030 % | 23°C / 50% RH; ISO 62 |
| 0.020 % @Time 86400 sec |
0.020 % @Time 24.0 hour |
50% RH; ASTM D 570 | |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0040 cm/cm @Time 86400 sec |
0.0020 - 0.0040 in/in @Time 24.0 hour |
ASTM D 955 |
| Linear Mold Shrinkage, Transverse | 0.0030 - 0.0050 cm/cm @Time 86400 sec |
0.0030 - 0.0050 in/in @Time 24.0 hour |
ASTM D 955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 66.0 MPa | 9570 psi | 5 mm/min; ISO 527 |
| 72.0 MPa | 10400 psi | Type I, 5 mm/min; ASTM D 638 | |
| Tensile Strength, Yield | 66.0 MPa | 9570 psi | 5 mm/min; ISO 527 |
| 72.0 MPa | 10400 psi | Type I, 5 mm/min; ASTM D 638 | |
| Elongation at Break | 1.2 % | 1.2 % | 5 mm/min; ISO 527 |
| 1.4 % | 1.4 % | Type I, 5 mm/min; ASTM D 638 | |
| Elongation at Yield | 1.2 % | 1.2 % | 5 mm/min; ISO 527 |
| 1.4 % | 1.4 % | Type I, 5 mm/min; ASTM D 638 | |
| Tensile Modulus | 7.79 GPa | 1130 ksi | 1 mm/min; ISO 527 |
| 8.34 GPa | 1210 ksi | 50 mm/min; ASTM D 638 | |
| Flexural Strength | 105 MPa | 15200 psi | ISO 178 |
| 108 MPa | 15700 psi | 1.3 mm/min, 50 mm span; ASTM D 790 | |
| Flexural Yield Strength | 112 MPa | 16200 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Flexural Modulus | 7.30 GPa | 1060 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| 7.55 GPa | 1100 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.250 J/cm @Temperature 23.0 °C |
0.468 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 2.11 J/cm @Temperature 23.0 °C |
3.95 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 2.00 kJ/m² @Temperature 23.0 °C |
0.952 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 13.0 kJ/m² @Temperature 23.0 °C |
6.19 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Impact Test | 1.00 J | 0.738 ft-lb | Multiaxial Impact; ISO 6603 |
| 8.00 J @Temperature 23.0 °C |
5.90 ft-lb @Temperature 73.4 °F |
Instrumented Impact Total Energy; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 226 °C | 439 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 244 °C @Thickness 3.20 mm |
471 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 117 °C | 243 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 123 °C @Thickness 3.20 mm |
253 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |