SABIC Innovative Plastics LNP VERTON UF-700-12 HS EXP PPA (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyphthalamide (PPA) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP VERTON |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP VERTON UF-700-12 HS EXP PPA (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Verton* UF-700-12 HS EXP is a compound based on Polyphthalamide resin containing Long Glass Fiber. Added features of this material include: Heat Stabilized.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.72 g/cc | 0.0621 lb/in³ | ASTM D792 |
| 1.72 g/cc | 0.0621 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.200 % | 0.200 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0018 cm/cm @Time 86400 sec |
0.0018 in/in @Time 24.0 hour |
ISO 294 |
| 0.0010 - 0.0030 cm/cm @Time 86400 sec |
0.0010 - 0.0030 in/in @Time 24.0 hour |
ASTM D955 | |
| Linear Mold Shrinkage, Transverse | 0.0045 cm/cm @Time 86400 sec |
0.0045 in/in @Time 24.0 hour |
ISO 294 |
| 0.0040 - 0.0060 cm/cm @Time 86400 sec |
0.0040 - 0.0060 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 216 MPa | 31300 psi | ISO 527 |
| 238 MPa | 34500 psi | ASTM D638 | |
| Tensile Strength, Yield | 238 MPa | 34500 psi | ASTM D638 |
| 238 MPa | 34500 psi | ISO 527 | |
| Elongation at Break | 1.2 % | 1.2 % | ISO 527 |
| 1.4 % | 1.4 % | ASTM D638 | |
| Elongation at Yield | 1.4 % | 1.4 % | ASTM D638 |
| 1.4 % | 1.4 % | ISO 527 | |
| Tensile Modulus | 22.24 GPa | 3226 ksi | 1 mm/min; ISO 527 |
| 22.75 GPa | 3300 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 341 MPa | 49500 psi | ISO 178 |
| 344 MPa | 49900 psi | ASTM D790 | |
| Flexural Modulus | 19.0 GPa | 2760 ksi | ISO 178 |
| 19.3 GPa | 2800 ksi | ASTM D790 | |
| Izod Impact, Notched | 2.24 J/cm | 4.20 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 8.86 J/cm | 16.6 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 28.0 kJ/m² | 13.3 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 46.0 kJ/m² | 21.9 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 14.0 J | 10.3 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 4.00 J | 2.95 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 28.8 µm/m-°C @Temperature -40.0 - 40.0 °C |
16.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 29.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
16.1 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 23.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
12.8 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 23.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
13.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 283 °C | 541 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 281 °C @Thickness 3.20 mm |
538 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 257 °C | 495 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 255 °C @Thickness 3.20 mm |
491 °F @Thickness 0.126 in |
unannealed; ASTM D648 |