SABIC Innovative Plastics LNP Verton NV006E PC/ABS

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Glass Fiber Filled , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP VERTON
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP Verton NV006E PC/ABS.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* Verton* NV006E is a compound based on PC/ABS resin containing Long Glass Fiber. Added features of this material include: Easy Molding.This data was supplied by SABIC-IP for the Americas region.
Physical Properties Metric English Comments
Density 1.35 g/cc
0.0488 lb/in³
ISO 1183
1.39 g/cc
0.0502 lb/in³
ASTM D 792
Moisture Absorption at Equilibrium 0.10 %

@Time 86400 sec
0.10 %

@Time 24.0 hour
50% RH; ASTM D 570
Linear Mold Shrinkage, Flow 0.0010 cm/cm

@Time 86400 sec
0.0010 in/in

@Time 24.0 hour
ASTM D 955
0.0011 cm/cm

@Time 86400 sec
0.0011 in/in

@Time 24.0 hour
ISO 294
Linear Mold Shrinkage, Transverse 0.0050 cm/cm

@Time 86400 sec
0.0050 in/in

@Time 24.0 hour
ASTM D 955
0.0052 cm/cm

@Time 86400 sec
0.0052 in/in

@Time 24.0 hour
ISO 294
Mechanical Properties Metric English Comments
Tensile Strength at Break 129 MPa
18700 psi
ASTM D 638
149 MPa
21600 psi
ISO 527
Tensile Strength, Yield 131 MPa
19000 psi
ASTM D 638
149 MPa
21600 psi
ISO 527
Elongation at Break 1.7 %
1.7 %
ASTM D 638
2.0 %
2.0 %
ISO 527
Elongation at Yield 1.6 %
1.6 %
ASTM D 638
2.0 %
2.0 %
ISO 527
Tensile Modulus 10.0 GPa
1450 ksi
1 mm/min; ISO 527
11.03 GPa
1600 ksi
50 mm/min; ASTM D 638
Flexural Strength 122 MPa
17700 psi
ISO 178
193 MPa
28000 psi
ASTM D 790
Flexural Modulus 8.27 GPa
1200 ksi
ASTM D 790
9.00 GPa
1310 ksi
ISO 178
Izod Impact, Notched 2.56 J/cm

@Temperature 23.0 °C
4.80 ft-lb/in

@Temperature 73.4 °F
ASTM D 256
Izod Impact, Notched (ISO) 25.0 kJ/m²

@Temperature 23.0 °C
11.9 ft-lb/in²

@Temperature 73.4 °F
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 48.0 kJ/m²

@Temperature 23.0 °C
22.8 ft-lb/in²

@Temperature 73.4 °F
80*10*4; ISO 180/1U
Impact Test 14.0 J

@Temperature 23.0 °C
10.3 ft-lb

@Temperature 73.4 °F
Instrumented Impact Energy @ peak; ASTM D 3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 41.4 µm/m-°C

@Temperature -40.0 - 40.0 °C
23.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
42.6 µm/m-°C

@Temperature -40.0 - 40.0 °C
23.7 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 52.2 µm/m-°C

@Temperature -40.0 - 40.0 °C
29.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
52.3 µm/m-°C

@Temperature -40.0 - 40.0 °C
29.1 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 143 °C

@Thickness 3.20 mm
289 °F

@Thickness 0.126 in
unannealed; ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 136 °C
277 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
135 °C

@Thickness 3.20 mm
275 °F

@Thickness 0.126 in
unannealed; ASTM D 648