SABIC Innovative Plastics LNP Verton RV008ESV_GY7E072 PA 66

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 40% Glass Fiber Filled
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP VERTON
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP Verton RV008ESV_GY7E072 PA 66.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Preliminary data for 40% long glass fiber filled, single color pellet gray, PA66This data was supplied by SABIC-IP for the Americas region.
Physical Properties Metric English Comments
Density 1.48 g/cc
0.0535 lb/in³
ISO 1183
1.485 g/cc
0.05365 lb/in³
ASTM D 792
Moisture Absorption at Equilibrium 0.65 %
0.65 %
23°C / 50% RH; ISO 62
0.93 %

@Time 86400 sec
 0.93 %

@Time 24.0 hour
 50% RH; ASTM D 570
Linear Mold Shrinkage, Flow 0.0023 - 0.0043 cm/cm

@Time 86400 sec
 0.0023 - 0.0043 in/in

@Time 24.0 hour
 ASTM D 955
Linear Mold Shrinkage, Transverse 0.0090 - 0.011 cm/cm

@Time 86400 sec
 0.0090 - 0.011 in/in

@Time 24.0 hour
 ASTM D 955
Mechanical Properties Metric English Comments
Tensile Strength at Break 182 MPa
26400 psi
Type I, 5 mm/min; ASTM D 638
195 MPa
28300 psi
5 mm/min; ISO 527
Tensile Strength, Yield 184 MPa
26700 psi
Type I, 5 mm/min; ASTM D 638
195 MPa
28300 psi
5 mm/min; ISO 527
Elongation at Break 2.0 %
2.0 %
Type I, 5 mm/min; ASTM D 638
2.3 %
2.3 %
5 mm/min; ISO 527
Elongation at Yield 2.1 %
2.1 %
Type I, 5 mm/min; ASTM D 638
2.3 %
2.3 %
5 mm/min; ISO 527
Tensile Modulus 10.44 GPa
1514 ksi
1 mm/min; ISO 527
11.56 GPa
1677 ksi
50 mm/min; ASTM D 638
Flexural Strength 273 MPa
39600 psi
1.3 mm/min, 50 mm span; ASTM D 790
276 MPa
40000 psi
2 mm/min; ISO 178
Flexural Modulus 10.19 GPa
1478 ksi
2 mm/min; ISO 178
11.3 GPa
1640 ksi
1.3 mm/min, 50 mm span; ASTM D 790
Izod Impact, Notched 2.23 J/cm

@Temperature -40.0 °C
 4.18 ft-lb/in

@Temperature -40.0 °F
 ASTM D 256
2.46 J/cm

@Temperature 23.0 °C
 4.61 ft-lb/in

@Temperature 73.4 °F
 ASTM D 256
Izod Impact, Unnotched 10.8 J/cm

@Temperature 23.0 °C
 20.2 ft-lb/in

@Temperature 73.4 °F
 ASTM D 4812
Izod Impact, Notched (ISO) 15.0 kJ/m²

@Temperature 23.0 °C
 7.14 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1A
27.0 kJ/m²

@Temperature -40.0 °C
 12.8 ft-lb/in²

@Temperature -40.0 °F
 80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 69.0 kJ/m²

@Temperature -40.0 °C
 32.8 ft-lb/in²

@Temperature -40.0 °F
 80*10*4; ISO 180/1U
71.0 kJ/m²

@Temperature 23.0 °C
 33.8 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1U
Impact Test 7.00 J

@Temperature 23.0 °C
 5.16 ft-lb

@Temperature 73.4 °F
 Instrumented Impact Energy @ peak; ASTM D 3763
16.0 J

@Temperature 23.0 °C
 11.8 ft-lb

@Temperature 73.4 °F
 Instrumented Impact Total Energy; ASTM D 3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 23.2 µm/m-°C

@Temperature -30.0 - 30.0 °C
 12.9 µin/in-°F

@Temperature -22.0 - 86.0 °F
 ASTM E 831
CTE, linear, Transverse to Flow 58.3 µm/m-°C

@Temperature -30.0 - 30.0 °C
 32.4 µin/in-°F

@Temperature -22.0 - 86.0 °F
 ASTM E 831
Deflection Temperature at 0.46 MPa (66 psi) 260 °C
500 °F
Flatw 80*10*4 sp=64mm; ISO 75/Bf
259 °C

@Thickness 3.20 mm
 498 °F

@Thickness 0.126 in
 unannealed; ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 256 °C
493 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
255 °C

@Thickness 3.20 mm
 491 °F

@Thickness 0.126 in
 unannealed; ASTM D 648