SABIC Innovative Plastics Lexan® BPL1000 PC (Asia Pacific)

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Lexan®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Lexan® BPL1000 PC (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Lexan* BPL1000 Polycarbonate (PC) resin is an injection moldable grade featuring high flow and good impact peroformance. It contains non-chlorinated and non-brominated flame retardant systems with UL-94 V0 rating at 0.8mm. Lexan BPL1000 resin offers various opaque color options and is ideal for thin wall applications.
Physical Properties Metric English Comments
Specific Gravity 1.16 g/cc
1.16 g/cc
ASTM D792
Density 1.20 g/cc
0.0434 lb/in³
ISO 1183
Water Absorption 0.15 %

@Time 86400 sec
0.15 %

@Time 24.0 hour
ASTM D570
Moisture Absorption 0.150 %
0.150 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.35 %
0.35 %
ISO 62
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm
0.0050 - 0.0070 in/in
on Tensile Bar; SABIC Method
0.0050 - 0.0070 cm/cm

@Thickness 3.20 mm
0.0050 - 0.0070 in/in

@Thickness 0.126 in
SABIC Method
Linear Mold Shrinkage, Transverse 0.0050 - 0.0070 cm/cm

@Thickness 3.20 mm
0.0050 - 0.0070 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 25.2 g/10 min

@Load 1.20 kg,
Temperature 300 °C
25.2 g/10 min

@Load 2.65 lb,
Temperature 572 °F
ASTM D1238
Melt Index of Compound 23 g/10 min

@Load 1.20 kg,
Temperature 300 °C
23 g/10 min

@Load 2.65 lb,
Temperature 572 °F
MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 51.0 MPa
7400 psi
Type I, 50 mm/min; ASTM D638
53.0 MPa
7690 psi
50 mm/min; ISO 527
Tensile Strength, Yield 58.0 MPa
8410 psi
SABIC - Japan Method
63.0 MPa
9140 psi
Type I, 50 mm/min; ASTM D638
64.0 MPa
9280 psi
50 mm/min; ISO 527
Elongation at Break 96.3 %
96.3 %
Type I, 50 mm/min; ASTM D638
96.8 %
96.8 %
50 mm/min; ISO 527
100 %
100 %
SABIC - Japan Method
Elongation at Yield 4.7 %
4.7 %
Type I, 50 mm/min; ASTM D638
4.7 %
4.7 %
50 mm/min; ISO 527
Tensile Modulus 2.46 GPa
357 ksi
1 mm/min; ISO 527
2.67 GPa
387 ksi
5 mm/min; ASTM D638
Flexural Strength 93.0 MPa
13500 psi
ASTM D790
Flexural Yield Strength 94.0 MPa
13600 psi
2 mm/min; ISO 178
102 MPa
14800 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 2.20 GPa
319 ksi
ASTM D790
2.36 GPa
342 ksi
2 mm/min; ISO 178
2.66 GPa
386 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 6.00 J/cm
11.2 ft-lb/in
ASTM D256
Izod Impact, Notched (ISO) 17.0 kJ/m²
8.09 ft-lb/in²
80*10*4; ISO 180/1A
12.0 kJ/m²

@Temperature -30.0 °C
5.71 ft-lb/in²

@Temperature -22.0 °F
80*10*4; ISO 180/1A
Charpy Impact, Notched 1.70 J/cm²
8.09 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 48.0 J

@Temperature 23.0 °C
35.4 ft-lb

@Temperature 73.4 °F
ASTM D3763
Thermal Properties Metric English Comments
CTE, linear 70.0 µm/m-°C

@Temperature -30.0 - 30.0 °C
38.9 µin/in-°F

@Temperature -22.0 - 86.0 °F
TMA
CTE, linear, Parallel to Flow 70.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
38.9 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
70.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
38.9 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 70.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
38.9 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
70.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
38.9 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 105 °C

@Thickness 3.20 mm
221 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 96.0 °C
205 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
Vicat Softening Point 111 °C
232 °F
Rate B/50; ASTM D1525
112 °C
234 °F
Rate B/50; ISO 306
114 °C
237 °F
Rate B/120; ISO 306
UL RTI, Electrical 80.0 °C
176 °F
UL 746B
UL RTI, Mechanical with Impact 80.0 °C
176 °F
UL 746B
UL RTI, Mechanical without Impact 80.0 °C
176 °F
UL 746B
Flammability, UL94 V-2

@Thickness 0.450 mm
V-2

@Thickness 0.0177 in
UL 94
V-0

@Thickness 0.800 mm
V-0

@Thickness 0.0315 in
UL 94
Oxygen Index 36 %
36 %
ISO 4589
Glow Wire Test 800 °C
1470 °F
IEC 60695-2-13
960 °C

@Thickness 1.00 mm
1760 °F

@Thickness 0.0394 in
IEC 60695-2-12
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
IEC 60093
Surface Resistance >= 1.00e+15 ohm
>= 1.00e+15 ohm
ROA; IEC 60093
Dielectric Constant 2.9

@Frequency 1.00e+6 Hz
2.9

@Frequency 1.00e+6 Hz
IEC 60250
3.0

@Frequency 50.0 - 60.0 Hz
3.0

@Frequency 50.0 - 60.0 Hz
IEC 60250
Dielectric Strength 27.0 kV/mm

@Thickness 1.60 mm
686 kV/in

@Thickness 0.0630 in
in oil; ASTM D149
Dissipation Factor 0.010

@Frequency 1.00e+6 Hz
0.010

@Frequency 1.00e+6 Hz
IEC 60250
0.030

@Frequency 50.0 - 60.0 Hz
0.030

@Frequency 50.0 - 60.0 Hz
IEC 60250
Comparative Tracking Index 200 V
200 V
IEC 60112
Descriptive Properties Value Comments
Ball Pressure Test, 75°C +/- 2°C PASS
IEC 60695-10-2