SABIC Innovative Plastics Lexan® BX9349 PC COPOLYMER (Asia Pacific)

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Lexan®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Lexan® BX9349 PC COPOLYMER (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Lexan* BX9349 resin is an injection moldable modified PC resin with non-brominated and non-chlorinated flame retardant to meet UL-94 V0 at 0.5mm and V2 at 0.4mm. Balanced flow with low temperature ductile together with the thin wall flame resistance, make it an ideal material of choice for a wide variety of thin wall applications
Physical Properties Metric English Comments
Specific Gravity 1.20 g/cc
1.20 g/cc
ASTM D792
Density 1.20 g/cc
0.0434 lb/in³
ISO 1183
Moisture Absorption 0.100 %
0.100 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.20 %
0.20 %
ISO 62
Linear Mold Shrinkage, Flow 0.0040 - 0.0060 cm/cm

@Thickness 3.20 mm
0.0040 - 0.0060 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 9.0 g/10 min

@Load 2.16 kg,
Temperature 260 °C
9.0 g/10 min

@Load 4.76 lb,
Temperature 500 °F
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 50.0 MPa
7250 psi
50 mm/min; ISO 527
Tensile Strength, Yield 65.0 MPa
9430 psi
50 mm/min; ISO 527
Elongation at Break 50 %
50 %
50 mm/min; ISO 527
Elongation at Yield 4.0 %
4.0 %
50 mm/min; ISO 527
Tensile Modulus 2.50 GPa
363 ksi
50 mm/min; ASTM D638
Flexural Yield Strength 90.0 MPa
13100 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 2.25 GPa
326 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 6.80 J/cm
12.7 ft-lb/in
ASTM D256
5.50 J/cm

@Temperature 0.000 °C
10.3 ft-lb/in

@Temperature 32.0 °F
ASTM D256
Dart Drop, Total Energy 65.0 J

@Temperature 23.0 °C
47.9 ft-lb

@Temperature 73.4 °F
ASTM D3763
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 106 °C

@Thickness 3.20 mm
223 °F

@Thickness 0.126 in
unannealed; ASTM D648
Vicat Softening Point 116 °C
241 °F
Rate B/120; ISO 306
UL RTI, Electrical 80.0 °C
176 °F
UL 746B
UL RTI, Mechanical with Impact 80.0 °C
176 °F
UL 746B
UL RTI, Mechanical without Impact 80.0 °C
176 °F
UL 746B
Flammability, UL94 V-2

@Thickness 0.400 mm
V-2

@Thickness 0.0157 in
UL 94
V-0

@Thickness 0.500 mm
V-0

@Thickness 0.0197 in
UL 94
Descriptive Properties Value Comments
Ball Pressure Test, 75°C +/- 2°C PASS
IEC 60695-10-2