SABIC Innovative Plastics Lexan® EM3110R PC

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Lexan®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Lexan® EM3110R PC.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Automotive interiors. Optimizes flow/processability for cost effective thinner wall design uses. Internal mold release.This data was supplied by SABIC-IP for the Americas region.
Physical Properties Metric English Comments
Specific Gravity 1.19 g/cc
1.19 g/cc
ASTM D 792
Water Absorption 0.16 %

@Time 86400 sec
0.16 %

@Time 24.0 hour
ASTM D 570
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm

@Thickness 3.20 mm
0.0050 - 0.0070 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 20 g/10 min

@Load 1.20 kg,
Temperature 300 °C
20 g/10 min

@Load 2.65 lb,
Temperature 572 °F
ASTM D 1238
Mechanical Properties Metric English Comments
Tensile Strength, Yield 55.0 MPa
7980 psi
Type I, 50 mm/min; ASTM D 638
Elongation at Break 90 %
90 %
Type I, 50 mm/min; ASTM D 638
Flexural Yield Strength 82.0 MPa
11900 psi
1.3 mm/min, 50 mm span; ASTM D 790
Flexural Modulus 2.17 GPa
315 ksi
1.3 mm/min, 50 mm span; ASTM D 790
Izod Impact, Notched 2.13 J/cm

@Temperature -30.0 °C
3.99 ft-lb/in

@Temperature -22.0 °F
ASTM D 256
5.87 J/cm

@Temperature -20.0 °C
11.0 ft-lb/in

@Temperature -4.00 °F
ASTM D 256
6.40 J/cm

@Temperature 23.0 °C
12.0 ft-lb/in

@Temperature 73.4 °F
ASTM D 256
2.13 J/cm

@Thickness 6.40 mm,
Temperature 23.0 °C
3.99 ft-lb/in

@Thickness 0.252 in,
Temperature 73.4 °F
ASTM D 256
Impact Test 56.0 J

@Temperature 23.0 °C
41.3 ft-lb

@Temperature 73.4 °F
Instrumented Impact Energy @ peak; ASTM D 3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 64.8 µm/m-°C

@Temperature -40.0 - 95.0 °C
36.0 µin/in-°F

@Temperature -40.0 - 203 °F
ASTM E 831
Deflection Temperature at 0.46 MPa (66 psi) 126 °C

@Thickness 6.40 mm
259 °F

@Thickness 0.252 in
unannealed; ASTM D 648
Deflection Temperature at 1.8 MPa (264 psi) 118 °C

@Thickness 3.20 mm
244 °F

@Thickness 0.126 in
unannealed; ASTM D 648
123 °C

@Thickness 6.40 mm
253 °F

@Thickness 0.252 in
unannealed; ASTM D 648