SABIC Innovative Plastics Lexan® EXL6414 PC

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Lexan®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Lexan® EXL6414 PC.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PC-Siloxane copolymer with excellent processability. Impact modified, medium flow, extreme low temp. ductility.
Physical Properties Metric English Comments
Specific Gravity 1.19 g/cc
1.19 g/cc
ASTM D792
Density 1.18 g/cc
0.0426 lb/in³
ISO 1183
Moisture Absorption 0.150 %
0.150 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.35 %
0.35 %
ISO 62
Linear Mold Shrinkage, Flow 0.0040 - 0.0080 cm/cm

@Thickness 3.20 mm
0.0040 - 0.0080 in/in

@Thickness 0.126 in
SABIC Method
Linear Mold Shrinkage, Transverse 0.0040 - 0.0080 cm/cm

@Thickness 3.20 mm
0.0040 - 0.0080 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 8.0 g/10 min

@Load 1.20 kg,
Temperature 300 °C
8.0 g/10 min

@Load 2.65 lb,
Temperature 572 °F
ASTM D1238
Melt Index of Compound 7.0 g/10 min

@Load 1.20 kg,
Temperature 300 °C
7.0 g/10 min

@Load 2.65 lb,
Temperature 572 °F
MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 58.0 MPa
8410 psi
50 mm/min; ISO 527
59.0 MPa
8560 psi
Type I, 50 mm/min; ASTM D638
Tensile Strength, Yield 54.0 MPa
7830 psi
50 mm/min; ISO 527
55.0 MPa
7980 psi
Type I, 50 mm/min; ASTM D638
Elongation at Break 88 %
88 %
50 mm/min; ISO 527
100 %
100 %
Type I, 50 mm/min; ASTM D638
Elongation at Yield 5.5 %
5.5 %
Type I, 50 mm/min; ASTM D638
6.0 %
6.0 %
50 mm/min; ISO 527
Tensile Modulus 1.72 GPa
249 ksi
50 mm/min; ASTM D638
2.27 GPa
329 ksi
1 mm/min; ISO 527
Flexural Yield Strength 79.0 MPa
11500 psi
1.3 mm/min, 50 mm span; ASTM D790
85.0 MPa
12300 psi
2 mm/min; ISO 178
Flexural Modulus 1.99 GPa
289 ksi
1.3 mm/min, 50 mm span; ASTM D790
2.09 GPa
303 ksi
2 mm/min; ISO 178
Izod Impact, Notched 8.01 J/cm
15.0 ft-lb/in
ASTM D256
6.94 J/cm

@Temperature -30.0 °C
13.0 ft-lb/in

@Temperature -22.0 °F
ASTM D256
Izod Impact, Unnotched 32.04 J/cm
60.02 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 70.0 kJ/m²
33.3 ft-lb/in²
80*10*3; ISO 180/1A
60.0 kJ/m²

@Temperature -30.0 °C
28.6 ft-lb/in²

@Temperature -22.0 °F
80*10*3; ISO 180/1A
Izod Impact, Unnotched (ISO) NB
NB
80*10*3; ISO 180/1U
NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
80*10*3; ISO 180/1U
Charpy Impact Unnotched NB
NB
Edgew 80*10*3 sp=62mm; ISO 179/1eU
NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
Edgew 80*10*3 sp=62mm; ISO 179/1eU
Charpy Impact, Notched 7.00 J/cm²
33.3 ft-lb/in²
Edgew 80*10*3 sp=62mm; ISO 179/1eA
6.00 J/cm²

@Temperature -30.0 °C
28.6 ft-lb/in²

@Temperature -22.0 °F
Edgew 80*10*3 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 61.0 J

@Temperature -30.0 °C
45.0 ft-lb

@Temperature -22.0 °F
ASTM D3763
62.0 J

@Temperature 23.0 °C
45.7 ft-lb

@Temperature 73.4 °F
ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 69.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
38.3 µin/in-°F

@Temperature 73.4 - 176 °F
ISO 11359-2
70.2 µm/m-°C

@Temperature -40.0 - 40.0 °C
39.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
CTE, linear, Transverse to Flow 72.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
40.0 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
73.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
40.6 µin/in-°F

@Temperature 73.4 - 176 °F
ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 136 °C
277 °F
Edgew 120*10*4 sp=100mm; ISO 75/Be
136 °C

@Thickness 3.20 mm
277 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 122 °C
252 °F
Edgew 120*10*4 sp=100mm; ISO 75/Ae
122 °C

@Thickness 3.20 mm
252 °F

@Thickness 0.126 in
unannealed; ASTM D648
Vicat Softening Point 140 °C
284 °F
Rate B/120; ISO 306
141 °C
286 °F
Rate B/50; ASTM D1525
141 °C
286 °F
Rate B/50; ISO 306
UL RTI, Electrical 80.0 °C
176 °F
UL 746B
UL RTI, Mechanical with Impact 80.0 °C
176 °F
UL 746B
UL RTI, Mechanical without Impact 80.0 °C
176 °F
UL 746B
Flammability, UL94 HB

@Thickness 1.47 mm
HB

@Thickness 0.0579 in
UL 94
Electrical Properties Metric English Comments
Volume Resistivity 1.70e+17 ohm-cm
1.70e+17 ohm-cm
IEC 60093
Surface Resistance 4.10e+17 ohm
4.10e+17 ohm
ROA; IEC 60093
Dielectric Constant 2.6

@Frequency 1.00e+6 Hz
2.6

@Frequency 1.00e+6 Hz
IEC 60250
Dielectric Strength 18.0 kV/mm

@Thickness 3.20 mm
457 kV/in

@Thickness 0.126 in
in oil; IEC 60243-1
Dissipation Factor 0.0094

@Frequency 1.00e+6 Hz
0.0094

@Frequency 1.00e+6 Hz
IEC 60250
Arc Resistance 120 - 180 sec
120 - 180 sec
Tungsten; ASTM D495
Comparative Tracking Index 175 - 250 V
175 - 250 V
UL 746A
Hot Wire Ignition, HWI 30 - 60 sec
30 - 60 sec
UL 746A
High Amp Arc Ignition, HAI >= 120 arcs
>= 120 arcs
UL 746A
High Voltage Arc-Tracking Rate, HVTR 80.0 - 150 mm/min
3.15 - 5.91 in/min
UL 746A
Descriptive Properties Value Comments
Ball Pressure Test, 125°C +/- 2°C PASSES
IEC 60695-10-2