Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Lexan®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Lexan® FXD941A PC.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
FXD153 is an Extrusion / Blow molding grade in a Diffusion effect, which is part of the VisualFX family. These effects have been developed to meet increasing Aesthetic demands in the Marketplace. Color Package may affect properties, Application testing always reccomended.
Physical Properties Metric English Comments
Specific Gravity 1.20 g/cc
1.20 g/cc
ASTM D792
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm

@Thickness 3.20 mm
0.0050 - 0.0070 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 2.5 g/10 min

@Load 1.20 kg,
Temperature 300 °C
2.5 g/10 min

@Load 2.65 lb,
Temperature 572 °F
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength at Break 66.0 MPa
9570 psi
Type I, 50 mm/min; ASTM D638
Tensile Strength, Yield 62.0 MPa
8990 psi
Type I, 50 mm/min; ASTM D638
Elongation at Break 110 %
110 %
Type I, 50 mm/min; ASTM D638
Elongation at Yield 7.0 %
7.0 %
Type I, 50 mm/min; ASTM D638
Tensile Modulus 2.34 GPa
339 ksi
5 mm/min; ASTM D638
Flexural Yield Strength 93.0 MPa
13500 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 2.34 GPa
339 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 7.48 J/cm
14.0 ft-lb/in
ASTM D256
Izod Impact, Unnotched 32.04 J/cm
60.02 ft-lb/in
ASTM D4812
Thermal Properties Metric English Comments
CTE, linear, Transverse to Flow 68.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
37.8 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
Deflection Temperature at 0.46 MPa (66 psi) 138 °C

@Thickness 3.20 mm
280 °F

@Thickness 0.126 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 132 °C

@Thickness 3.20 mm
270 °F

@Thickness 0.126 in
unannealed; ASTM D648
Vicat Softening Point 157 °C
315 °F
Rate B/50; ASTM D1525