SABIC Innovative Plastics Lexan® FXG1413T PC Copolymer (Asia Pacific)

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Lexan®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Lexan® FXG1413T PC Copolymer (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PC-siloxane copolymer in special ""Diamond Sparkle"" colors. Medium flow. Improved toughness compared to medium flow standard PC in same color. Color package may affect performance.
Physical Properties Metric English Comments
Specific Gravity 1.18 g/cc
1.18 g/cc
ASTM D792
Density 1.18 g/cc
0.0426 lb/in³
ISO 1183
Moisture Absorption 0.0900 %
0.0900 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.12 %
0.12 %
ISO 62
Linear Mold Shrinkage, Flow 0.0040 - 0.0080 cm/cm
0.0040 - 0.0080 in/in
on Tensile Bar; SABIC Method
0.0040 - 0.0080 cm/cm

@Thickness 3.20 mm
0.0040 - 0.0080 in/in

@Thickness 0.126 in
SABIC Method
Linear Mold Shrinkage, Transverse 0.0040 - 0.0080 cm/cm

@Thickness 3.20 mm
0.0040 - 0.0080 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 10 g/10 min

@Load 1.20 kg,
Temperature 300 °C
10 g/10 min

@Load 2.65 lb,
Temperature 572 °F
ASTM D1238
Melt Index of Compound 9.0 g/10 min

@Load 1.20 kg,
Temperature 300 °C
9.0 g/10 min

@Load 2.65 lb,
Temperature 572 °F
MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 46.0 MPa
6670 psi
50 mm/min; ISO 527
47.0 MPa
6820 psi
Type I, 50 mm/min; ASTM D638
Tensile Strength, Yield 57.0 MPa
8270 psi
50 mm/min; ISO 527
59.0 MPa
8560 psi
Type I, 50 mm/min; ASTM D638
Elongation at Break 38 %
38 %
50 mm/min; ISO 527
69 %
69 %
Type I, 50 mm/min; ASTM D638
Elongation at Yield 5.6 %
5.6 %
50 mm/min; ISO 527
6.0 %
6.0 %
Type I, 50 mm/min; ASTM D638
Tensile Modulus 2.27 GPa
329 ksi
50 mm/min; ASTM D638
2.33 GPa
338 ksi
1 mm/min; ISO 527
Flexural Yield Strength 85.0 MPa
12300 psi
1.3 mm/min, 50 mm span; ASTM D790
90.0 MPa
13100 psi
2 mm/min; ISO 178
Flexural Modulus 2.19 GPa
318 ksi
2 mm/min; ISO 178
2.27 GPa
329 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 5.70 J/cm
10.7 ft-lb/in
ASTM D256
3.76 J/cm

@Temperature -30.0 °C
7.04 ft-lb/in

@Temperature -22.0 °F
ASTM D256
Izod Impact, Notched (ISO) 36.0 kJ/m²
17.1 ft-lb/in²
80*10*4; ISO 180/1A
16.0 kJ/m²

@Temperature -30.0 °C
7.61 ft-lb/in²

@Temperature -22.0 °F
80*10*4; ISO 180/1A
Charpy Impact, Notched 1.90 J/cm²
9.04 ft-lb/in²
Edgew 80*10*4 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 54.0 J

@Temperature 23.0 °C
39.8 ft-lb

@Temperature 73.4 °F
ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 71.5 µm/m-°C

@Temperature 23.0 - 80.0 °C
39.7 µin/in-°F

@Temperature 73.4 - 176 °F
ISO 11359-2
71.5 µm/m-°C

@Temperature -40.0 - 95.0 °C
39.7 µin/in-°F

@Temperature -40.0 - 203 °F
ASTM E 831
CTE, linear, Transverse to Flow 79.3 µm/m-°C

@Temperature 23.0 - 80.0 °C
44.1 µin/in-°F

@Temperature 73.4 - 176 °F
ISO 11359-2
79.3 µm/m-°C

@Temperature -40.0 - 95.0 °C
44.1 µin/in-°F

@Temperature -40.0 - 203 °F
ASTM E 831
Deflection Temperature at 1.8 MPa (264 psi) 119 °C
246 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
123 °C

@Thickness 3.20 mm
253 °F

@Thickness 0.126 in
unannealed; ASTM D648
Vicat Softening Point 141 °C
286 °F
Rate B/50; ISO 306
142 °C
288 °F
Rate B/50; ASTM D1525
143 °C
289 °F
Rate B/120; ISO 306
Descriptive Properties Value Comments
Ball Pressure Test, 75°C +/- 2°C PASS
IEC 60695-10-2