SABIC Innovative Plastics Lexan® FXM4701 PPC (Asia Pacific)

Category Polymer , Thermoplastic , Polyphthalate Carbonate
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Lexan®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Lexan® FXM4701 PPC (Asia Pacific).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LEXAN FMX4701 is a high heat resistant poly(ester)carbonate injection molding resin. This grade is especially designed to visualize color effects.This data was supplied by SABIC-IP for the Asia Pacific region.
Physical Properties Metric English Comments
Specific Gravity 1.20 g/cc
1.20 g/cc
ASTM D 792
Density 1.20 g/cc
0.0434 lb/in³
ISO 1183
Moisture Absorption at Equilibrium 0.15 %
0.15 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.35 %

@Temperature 23.0 °C
0.35 %

@Temperature 73.4 °F
ISO 62
Linear Mold Shrinkage, Flow 0.0080 - 0.010 cm/cm

@Thickness 3.20 mm
0.0080 - 0.010 in/in

@Thickness 0.126 in
SABIC Method
Linear Mold Shrinkage, Transverse 0.0080 - 0.010 cm/cm

@Thickness 3.20 mm
0.0080 - 0.010 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 2.0 g/10 min

@Load 1.20 kg,
Temperature 300 °C
2.0 g/10 min

@Load 2.65 lb,
Temperature 572 °F
ASTM D 1238
6.0 g/10 min

@Load 5.00 kg,
Temperature 300 °C
6.0 g/10 min

@Load 11.0 lb,
Temperature 572 °F
[cm^3/10 min] Melt Volume Rate; ISO 1133
8.0 g/10 min

@Load 2.16 kg,
Temperature 330 °C
8.0 g/10 min

@Load 4.76 lb,
Temperature 626 °F
[cm^3/10 min] Melt Volume Rate; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 64.0 MPa
9280 psi
50 mm/min; ISO 527
78.0 MPa
11300 psi
Type I, 50 mm/min; ASTM D 638
Tensile Strength, Yield 66.0 MPa
9570 psi
Type I, 50 mm/min; ASTM D 638
70.0 MPa
10200 psi
50 mm/min; ISO 527
Elongation at Break >= 50 %
>= 50 %
Type I, 50 mm/min; ASTM D 638
>= 50 %
>= 50 %
50 mm/min; ISO 527
Elongation at Yield 6.0 %
6.0 %
Type I, 50 mm/min; ASTM D 638
7.0 %
7.0 %
50 mm/min; ISO 527
Tensile Modulus 2.25 GPa
326 ksi
5 mm/min; ASTM D 638
2.30 GPa
334 ksi
1 mm/min; ISO 527
Flexural Yield Strength 97.0 MPa
14100 psi
1.3 mm/min, 50 mm span; ASTM D 790
100 MPa
14500 psi
2 mm/min; ISO 178
Flexural Modulus 2.30 GPa
334 ksi
2 mm/min; ISO 178
2.35 GPa
341 ksi
1.3 mm/min, 50 mm span; ASTM D 790
Izod Impact, Notched 3.00 J/cm

@Temperature 23.0 °C
5.62 ft-lb/in

@Temperature 73.4 °F
ASTM D 256
Izod Impact, Unnotched NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
ASTM D 4812
Izod Impact, Notched (ISO) 10.0 kJ/m²

@Temperature -30.0 °C
4.76 ft-lb/in²

@Temperature -22.0 °F
80*10*4; ISO 180/1A
12.0 kJ/m²

@Temperature 23.0 °C
5.71 ft-lb/in²

@Temperature 73.4 °F
80*10*4; ISO 180/1A
Charpy Impact, Notched 1.50 J/cm²

@Temperature 23.0 °C
7.14 ft-lb/in²

@Temperature 73.4 °F
V-notch Edgew 80*10*4 sp=62mm; ISO 179/1eA
Impact Test 54.0 J

@Temperature 23.0 °C
39.8 ft-lb

@Temperature 73.4 °F
Instrumented Impact Total Energy; ASTM D 3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 80.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
44.4 µin/in-°F

@Temperature 73.4 - 176 °F
ISO 11359-2
80.0 µm/m-°C

@Temperature -40.0 - 95.0 °C
44.4 µin/in-°F

@Temperature -40.0 - 203 °F
ASTM E 831
CTE, linear, Transverse to Flow 80.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
44.4 µin/in-°F

@Temperature 73.4 - 176 °F
ISO 11359-2
80.0 µm/m-°C

@Temperature -40.0 - 95.0 °C
44.4 µin/in-°F

@Temperature -40.0 - 203 °F
ASTM E 831
Deflection Temperature at 0.46 MPa (66 psi) 165 °C
329 °F
Edgew 120*10*4 sp=100mm; ISO 75/Be
Deflection Temperature at 1.8 MPa (264 psi) 150 °C
302 °F
Edgew 120*10*4 sp=100mm; ISO 75/Ae
149 °C

@Thickness 3.20 mm
300 °F

@Thickness 0.126 in
unannealed; ASTM D 648
Vicat Softening Point 170 °C
338 °F
Rate B/120; ISO 306
175 °C
347 °F
Rate B/50; ISO 306
185 °C
365 °F
Rate B/50; ASTM D 1525
Descriptive Properties Value Comments
Ball Pressure Test, 125°C +/- 2°C PASSES
IEC 60695-10-2