SABIC Innovative Plastics Lexan® HPS4 PC

Category Polymer , Thermoplastic , Polycarbonate (PC)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Lexan®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Lexan® HPS4 PC.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Medium flow polycarbonate. For medical devices and pharmaceutical applications. Healthcare management of change, biocompatible (ISO10993 or USP Class VI).EtO, steam, e-beam, and gamma sterilizable. Contains mold release.
Physical Properties Metric English Comments
Specific Gravity 1.19 g/cc
1.19 g/cc
ASTM D792
Density 1.19 g/cc
0.0430 lb/in³
ISO 1183
Water Absorption 0.14 %

@Time 86400 sec
0.14 %

@Time 24.0 hour
ASTM D570
Moisture Absorption 0.100 %
0.100 %
23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.26 %
0.26 %
ISO 62
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm
0.0050 - 0.0070 in/in
on Tensile Bar; SABIC Method
0.0050 - 0.0070 cm/cm

@Thickness 3.20 mm
0.0050 - 0.0070 in/in

@Thickness 0.126 in
SABIC Method
Linear Mold Shrinkage, Transverse 0.0050 - 0.0070 cm/cm

@Thickness 3.20 mm
0.0050 - 0.0070 in/in

@Thickness 0.126 in
SABIC Method
Melt Flow 10.5 g/10 min

@Load 1.20 kg,
Temperature 300 °C
10.5 g/10 min

@Load 2.65 lb,
Temperature 572 °F
ASTM D1238
Melt Index of Compound 10 g/10 min

@Load 1.20 kg,
Temperature 300 °C
10 g/10 min

@Load 2.65 lb,
Temperature 572 °F
MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 73.0 MPa
10600 psi
50 mm/min; ISO 527
74.0 MPa
10700 psi
Type I, 50 mm/min; ASTM D638
Tensile Strength, Yield 61.0 MPa
8850 psi
50 mm/min; ISO 527
62.0 MPa
8990 psi
Type I, 50 mm/min; ASTM D638
Elongation at Break 128 %
128 %
50 mm/min; ISO 527
140 %
140 %
Type I, 50 mm/min; ASTM D638
Elongation at Yield 6.0 %
6.0 %
50 mm/min; ISO 527
6.5 %
6.5 %
Type I, 50 mm/min; ASTM D638
Tensile Modulus 2.30 GPa
334 ksi
50 mm/min; ASTM D638
2.39 GPa
347 ksi
1 mm/min; ISO 527
Flexural Yield Strength 93.0 MPa
13500 psi
2 mm/min; ISO 178
100 MPa
14500 psi
1.3 mm/min, 50 mm span; ASTM D790
Flexural Modulus 2.25 GPa
326 ksi
2 mm/min; ISO 178
2.40 GPa
348 ksi
1.3 mm/min, 50 mm span; ASTM D790
Izod Impact, Notched 8.40 J/cm
15.7 ft-lb/in
ASTM D256
2.20 J/cm

@Temperature -30.0 °C
4.12 ft-lb/in

@Temperature -22.0 °F
ASTM D256
Izod Impact, Notched (ISO) 70.0 kJ/m²
33.3 ft-lb/in²
80*10*3; ISO 180/1A
10.0 kJ/m²

@Temperature -30.0 °C
4.76 ft-lb/in²

@Temperature -22.0 °F
80*10*3; ISO 180/1A
Izod Impact, Unnotched (ISO) NB
NB
80*10*3; ISO 180/1U
NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
80*10*3; ISO 180/1U
Charpy Impact Unnotched NB
NB
Edgew 80*10*3 sp=62mm; ISO 179/1eU
NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
Edgew 80*10*3 sp=62mm; ISO 179/1eU
Charpy Impact, Notched 7.00 J/cm²
33.3 ft-lb/in²
Edgew 80*10*3 sp=62mm; ISO 179/1eA
8.20 J/cm²
39.0 ft-lb/in²
ISO 179/2C
1.50 J/cm²

@Temperature -30.0 °C
7.14 ft-lb/in²

@Temperature -22.0 °F
Edgew 80*10*3 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 88.0 J

@Temperature 23.0 °C
64.9 ft-lb

@Temperature 73.4 °F
ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 78.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
43.3 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
78.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
43.3 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
CTE, linear, Transverse to Flow 76.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
42.2 µin/in-°F

@Temperature -40.0 - 104 °F
ASTM E 831
76.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
42.2 µin/in-°F

@Temperature -40.0 - 104 °F
ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi) 138 °C

@Thickness 6.40 mm
280 °F

@Thickness 0.252 in
unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 127 °C
261 °F
Edgew 120*10*4 sp=100mm; ISO 75/Ae
126 °C

@Thickness 3.20 mm
259 °F

@Thickness 0.126 in
unannealed; ASTM D648
132 °C

@Thickness 6.40 mm
270 °F

@Thickness 0.252 in
unannealed; ASTM D648
Vicat Softening Point 143 °C
289 °F
Rate B/50; ASTM D1525
143 °C
289 °F
Rate B/50; ISO 306
145 °C
293 °F
Rate B/120; ISO 306
Descriptive Properties Value Comments
Ball Pressure Test, 125°C +/- 2°C PASSES
IEC 60695-10-2